Method for making nanoscale channels
A method of making nanoscale channels including: providing a substrate, locating a photoresist mask layer on the substrate, the thickness of the photoresist mask layer equals H; forming a patterned mask layer by exposing and developing the photoresist mask layer, the patterned mask layer includes a plurality of parallel and spaced stripe masks, the spacing between adjacent stripe masks equals L; depositing a first thin film layer on the substrate in a first direction, the thickness of the first thin film layer equals D, a first angle between the first direction and a direction in the thickness of the stripe masks equals θ 1 , θ 1 <tan −1 (L/H); depositing a second thin film layer on the substrate in a second direction, a second angle between the second direction and the direction in the thickness of the stripe masks equals θ 2 , θ 2 <tan −1 [L/(H+D)], 0<Htanθ 1 +(H+D)tanθ 2 −L<10 nm.
1. A method of making nanoscale channels, comprising:
locating a photoresist mask layer on a substrate, wherein a first thickness of the photoresist mask layer equals H;
forming a patterned mask layer by exposing and developing the photoresist mask layer, wherein the patterned mask layer comprises a plurality of parallel and spaced stripe masks, a spacing between adjacent stripe masks equals L, a top surface of the patterned mask layer away from the substrate defines a first area I, a side surface of the patterned mask layer defines a second area II, a surface of the substrate exposed between adjacent stripe masks defines a third area III;
depositing a first thin film layer on the substrate in a first direction, a second thickness of the first thin film layer equals D, a first angle between the first direction and a thickness direction of the stripe masks equals a first angle θ 1 , θ 1 <tan −1 (L/H);
depositing a second thin film layer on the substrate in a second direction, a second angle between the second direction and the thickness direction of the stripe masks equals a second angle θ 2 , θ 2 <tan −1 [L/(H+D)], 0<Htanθ 1 +(H+D)tanθ 2 −L<10 nm, the entire second area II is covered by the first thin film layer and the second thin film layer, an interval area between the first thin film layer and the second thin film layer is formed in the third area III and forms a nanoscale channel.
2. The method as claimed in claim 1 , wherein the thickness H of the photoresist mask layer is in a range of 200 nanometers to 400 nanometers.
3. The method as claimed in claim 1 , wherein the spacing L between adjacent stripe masks is in a range of 200 nanometers to 450 nanometers.
4. The method as claimed in claim 1 , wherein the first angle θ 1 between the first direction and the thickness direction of the stripe masks is less than or equal to 45 degrees.
5. The method as claimed in claim 1 , wherein the thickness D of the first thin film layer is less than 40 nanometers.
6. The method as claimed in claim 1 , wherein the second angle θ 2 between the second direction and the thickness direction of the stripe masks is less than or equal to 45 degrees.
7. The method as claimed in claim 1 , wherein an extending direction of the stripe masks is perpendicular to both the first direction and the second direction.
8. A method of making nanoscale channels, comprising:
locating a photoresist mask layer on a substrate, wherein a first thickness of the photoresist mask layer equals H;
forming a patterned mask layer by exposing and developing the photoresist mask layer, wherein the patterned mask layer comprises a plurality of parallel and spaced stripe masks, a spacing between adjacent stripe masks equals L, a top surface of the patterned mask layer away from the substrate defines a first area I, a side surface of the patterned mask layer defines a second area II, a surface of the substrate exposed between adjacent stripe masks defines a third area III;
rotating the substrate with an extending direction of the stripe masks as a rotation axis, a first angle between the substrate and the horizontal direction equals a first angle θ 1 , θ 1 <tan −1 (L/H), depositing a first thin film layer on the substrate in the vertical direction, a second thickness of the first thin film layer equals D;
rotating the substrate back to the horizontal direction, continuing to rotate the substrate to obtain a second angle, the second angle between the substrate and the horizontal direction equals a second angle θ 2 , θ 2 <tan −1 [L/(H+D)], depositing a second thin film layer on the substrate in the vertical direction, 0<Htanθ 1 +(H+D)tanθ 2 −L<10 nm, an interval area between the first thin film layer and the second thin film layer is formed in the third area III and forms a nanoscale channel.
9. The method as claimed in claim 8 , wherein the first thin film layer and the second thin film layer are deposited vertically upward on the substrate.
10. The method as claimed in claim 8 , wherein the first thin film layer and the second thin film layer are deposited vertically downward on the substrate.
11. The method as claimed in claim 8 , wherein the first angle θ 1 is less than or equal to 45 degrees.
12. The method as claimed in claim 8 , wherein the second angle θ 2 is less than or equal to 45 degrees.
13. The method as claimed in claim 8 , wherein spacing L between adjacent stripe masks is in a range of 200 nanometers to 450 nanometers.
14. The method as claimed in claim 8 , wherein the thickness H of the photoresist mask layer is in a range of 200 nanometers to 400 nanometers.
15. The method as claimed in claim 8 , wherein the thickness D of the first thin film layer is less than 40 nanometers.