Method for manufacturing zeolite membrane structure
A method for manufacturing a zeolite membrane structure includes a step of forming a first zeolite membrane on a porous support by hydrothermal synthesis in a state in which the porous support is immersed in a first zeolite membrane formation solution, a step of immersing the porous support formed the first zeolite membrane for greater than or equal to 5 minutes in a second zeolite membrane formation solution at greater than or equal to 10 degrees C. and less than or equal to 70 degrees C. and greater than or equal to pH 10, and a step of forming a second zeolite membrane on the first zeolite membrane by hydrothermal synthesis in a state in which the porous support formed the first zeolite membrane is immersed in the second zeolite membrane formation solution. The first zeolite membrane and the second zeolite membrane share at least one composite building unit constituting a framework structure.
1. A method for manufacturing a zeolite membrane structure comprising:
a step of forming a first zeolite membrane on a porous support by hydrothermal synthesis in a state in which the porous support is immersed in a first zeolite membrane formation solution,
a step of immersing the porous support and the first zeolite membrane formed on the porous support for greater than or equal to 1 hour in a second zeolite membrane formation solution at greater than or equal to 10 degrees C. and less than or equal to 70 degrees C. and greater than or equal to pH10 so as to activate an exposed surface of the first zeolite membrane, and
a step of forming a second zeolite membrane on the first zeolite membrane by hydrothermal synthesis in a state in which the porous support and the first zeolite membrane formed on the porous support are immersed in the second zeolite membrane formation solution,
the first zeolite membrane and the second zeolite membrane sharing at least one composite building unit constituting a framework structure,
wherein the step of immersing the porous support and the first zeolite membrane formed on the porous support is performed before the step of forming the second zeolite membrane on the first zeolite membrane by hydrothermal synthesis.
2. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein
a content amount of second zeolite membrane forming seed crystals in the second zeolite membrane formation solution is less than or equal to 0.1 wt %.
3. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein
a mass per unit surface area of the second zeolite forming seed crystals attached on a surface of the first zeolite membrane is less than or equal to 0.01 g/cm 2 .
4. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein
after formation of the second zeolite membrane, a weight of the second zeolite membrane is greater than a total weight of second zeolite precipitated in the second zeolite membrane formation solution.
5. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein
a framework structure of the first zeolite membrane is the same as a framework structure of the second zeolite membrane.
6. The method for manufacturing a zeolite membrane structure according to claim 5 , wherein
the Si/Al atomic ratio in the first zeolite membrane is different from the Si/Al atomic ratio in the second zeolite membrane.
7. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein
a framework structure of at least one of the first zeolite membrane and the second zeolite membrane is any of MFI, DDR, MEL, BEA, CHA, MOR, FAU, LTA, FER, and SOD.
8. The method for manufacturing a zeolite membrane structure according to claim 1 , wherein the temperature range of the second zeolite membrane formation solution is greater than or equal to 10 degrees C. and less than or equal to 30 degrees C.