Argon addition to remote plasma oxidation
Methods for conformal radical oxidation of structures are provided. In one implementation, the method comprises flowing hydrogen into a processing chamber at a first flow rate, wherein the processing chamber has a substrate positioned therein. The method further comprises flowing oxygen into a precursor activator at a second flow rate. The method further comprises flowing argon into the precursor activator at a third flow rate. The method further comprises generating a plasma in the precursor activator from the oxygen and argon. The method further comprises flowing the plasma into the processing chamber, wherein the plasma mixes with the hydrogen gas to create an activated processing gas. The method further comprises exposing the substrate to the activated gas to form an oxide film on the substrate. A growth rate of the oxide film is controlled by adjusting the third flow rate.
1. A method for oxidation, comprising:
flowing hydrogen gas into a processing region of a processing chamber at a first flow rate, wherein the processing region has a substrate positioned therein;
flowing oxygen gas into a precursor activator at a second flow rate;
flowing argon gas into the precursor activator at a third flow rate;
generating a plasma in the precursor activator from the oxygen gas and the argon gas;
flowing the plasma into the processing region, wherein the plasma mixes with the hydrogen gas to create an activated processing gas; and
exposing the substrate to the activated processing gas to form an oxide film on the substrate, wherein a growth rate of the oxide film is controlled by adjusting the third flow rate.
2. The method of claim 1 , further comprising increasing the third flow rate to increase the growth rate of the oxide film.
3. The method of claim 1 , further comprising decreasing the third flow rate to decrease the growth rate of the oxide film.
4. The method of claim 1 , wherein a ratio of the second flow rate to the third flow rate (O 2 :Ar) is between about 1:1 and about 5:1.
5. The method of claim 1 , further comprising flowing oxygen gas and/or argon gas into the processing region prior to flowing the plasma into the processing region.
6. The method of claim 5 , wherein the substrate is maintained at a temperature between 500 degrees Celsius and 1100 degrees Celsius.
7. The method of claim 6 , wherein the processing region is maintained at a pressure between about 0.5 Torr and about 5 Torr.
8. The method of claim 5 , wherein a concentration of argon gas in the precursor activator, based on a total amount of the argon gas and the oxygen gas, is between 20 percent and 50 percent.
9. The method of claim 1 , further comprising flowing hydrogen gas into the precursor activator at a fourth flow rate prior to generating the plasma.
10. The method of claim 1 , wherein the substrate comprises at least one of an exposed silicon nitride surface, an exposed polysilicon surface, an exposed alumina surface, and an exposed silicon oxide surface.