Seam-healing method upon supra-atmospheric process in diffusion promoting ambient
Aspects of the disclosure include methods of treating a substrate to remove one or more of voids, seams, and grain boundaries from interconnects formed on the substrate. The method includes heating the substrate in an environment pressurized at supra-atmospheric pressure. In one example, the substrate may be heated in a hydrogen-containing atmosphere.
1. A method of processing a substrate comprising:
depositing a conductive material on the substrate to form an interconnect having one or more seams or voids are formed therein, the conductive material comprising cobalt or ruthenium;
heating the substrate to a predetermined temperature, wherein the predetermined temperature is below a melting point of the conductive material; and
healing the one or more seams or voids by exposing the interconnect to a hydrogen-containing atmosphere at a pressure between about 1 bar and about 50 bar.
2. The method of claim 1 , wherein the predetermined temperature is between about 300 degrees Celsius and about 400 degrees Celsius.
3. The method of claim 1 , wherein the hydrogen-containing atmosphere includes hydrogen present within a range of about 1 atomic percent to about 100 atomic percent.
4. The method of claim 1 , wherein the hydrogen-containing atmosphere comprises deuterium.
5. The method of claim 1 , wherein the exposing weakens surface bonds of the conductive material.
6. The method of claim 1 , wherein healing the one or more seams or voids further comprises reducing the grain boundaries.
7. A method of processing a substrate comprising:
depositing a conductive material on the substrate to form an interconnect having one or more seams or voids are formed therein, the conductive material comprising cobalt or ruthenium; and
healing the one or more seams or voids, wherein healing the one or more seams or voids comprises:
exposing the interconnect to a deuterium atmosphere at a pressure between about 1 bar and about 50 bar; and
heating the substrate to a predetermined temperature, wherein the predetermined temperature is below a melting point of the conductive material.
8. The method of claim 7 , wherein the predetermined temperature is between about 250 degrees Celsius and about 400 degrees Celsius.
9. The method of claim 7 , wherein the deuterium atmosphere has deuterium in a range between about 2 atomic percent to about 5 atomic percent.
10. The method of claim 7 , wherein the exposing further comprises hydrogen, and wherein the exposing causes weakening of surface bonds of the conductive material.
11. The method of claim 7 , wherein healing the one or more seams or voids further comprises reducing the grain boundaries.
12. A method of processing a substrate comprising:
positioning a substrate in a processing chamber, the substrate having an interconnect formed from a conductive material formed thereon, the conductive material comprising cobalt or ruthenium, wherein one or more seams or voids are present in the interconnect; and
healing the one or more seams or voids, wherein healing the one or more seams or voids simultaneously comprises:
exposing the interconnect to a hydrogen-containing environment at a supra-atmospheric pressure; and
heating the substrate to a predetermined temperature, wherein the predetermined temperature is below a melting point of the conductive material.
13. The method of claim 12 , wherein the predetermined temperature is between about 250 degrees Celsius and about 400 degrees Celsius.
14. The method of claim 12 , wherein the supra-atmospheric pressure is between about 12 bar and about 50 bar.
15. The method of claim 12 , wherein the hydrogen-containing environment includes hydrogen present within a range of about 1 atomic percent to about 100 atomic percent.
16. The method of claim 15 , wherein the hydrogen-containing environment further contains deuterium.
17. The method of claim 12 , wherein the exposing weakens surface bonds of the conductive material.
18. The method of claim 12 , wherein healing the one or more seams or voids further comprises reducing the grain boundaries.
19. The method of claim 12 , wherein the healing the one or more seams or voids facilitates movement of the conductive material.
20. The method of claim 12 , wherein the healing the one or more seams or voids removes contaminates from the seams or voids.