Multicomponent meso thread containing hyaluronic acid and method for producing same (variants)
The group of inventions relates to the field of aesthetic, plastic and reconstructive cosmetology/medicine, and more particularly to meso threads used for remedying aesthetic and age-related changes to the skin, and to methods for producing such threads. Proposed is a multicomponent meso thread consisting of a core and a shell. The core is realized in the form of a fibroin thread, and the shell contains hyaluronic acid or a salt thereof or a polyelectrolyte complex of hyaluronic acid or a salt thereof and chitosan or a salt thereof. Also proposed are a variant of the thread having a plastifying agent in the shell, and methods for producing the proposed meso threads.
1. A method for producing a multicomponent mesothread consisting of a core and a coating, wherein the core is a fibroin thread, comprising:
a. preparing a forming solution of hyaluronic acid or its salt as follows:
i. swelling and dissolving of hyaluronic acid or its salt in water;
ii. adding to the obtained solution 10 to 40 mass % of ethyl alcohol with respect to weight of the obtained solution; and
iii. ripening and deaerating the obtained solution by ageing for 22±2 hours at the temperature of 22±2° C.;
b. drawing the fibroin thread through the forming solution and a calibrated nozzle; and
c. drying.
2. The method according to claim 1 , wherein said hyaluronic acid salt comprises at least one of tetraalkylammonium, lithium, sodium, potassium, calcium, magnesium, barium, zinc, aluminum, copper, aurate, and hyaluronic acid hydrosalt.
3. The method according to claim 1 , wherein an antiinfection agent is additionally introduced into the forming solution of hyaluronic acid or its salt, wherein the antiinfection agent comprises beta-(5-nitrofuril-2)-acrolein.
4. The method according to claim 1 , wherein an antiseptic agent is additionally introduced into the forming solution of hyaluronic acid or its salt, wherein the antiseptic agent comprises benzyldimethyl [3-(myristoylamino)propyl] ammonium chloride monohydrate.
5. The method according to claim 1 , further comprising the steps of drawing the thread through a previously prepared forming solution of chitosan or its salt, drawing the obtained thread through a calibrated nozzle and drying.
6. The method according to claim 5 , wherein the forming solution of chitosan or its salt is prepared by the following steps: swelling and dissolving of chitosan or its salt in water; mixing the obtained solution gradually with an amount of concentrated acetic acid equal to the amount of chitosan; after the chitosan is dissolved, adding to the obtained solution 10 to 40 mass % of ethyl alcohol with respect to weight of the obtained solution; and ripening the obtained solution by ageing for 22±2 hours at the temperature of 22±2° C.
7. The method according to claim 5 , wherein the chitosan comprises a chitosan with deacetylation degree over 50%, and the chitosan salt comprises chitosan acetate, chitosan chloride, or chitosan lactate.
8. The method according to claim 5 , wherein a coupling agent is additionally introduced into the forming solution of chitosan, wherein the coupling agent comprises genipin.
9. The method according to claim 5 , wherein a coupling agent is additionally introduced into the forming solution of chitosan, wherein the coupling agent is selected from the group consisting of: ethyleneglycol diglycidyl ether, diethyleneglycol diglycidyl ether, triethyleneglycol diglycidyl ether, polyethyleneglycol diglycidyl ether, propyleneglycol diglycidyl ether, 1,4-butanediol diglycidyl ether, and 1,6-hexandiol diglycidyl ether.
10. The method according to claim 5 , wherein a coupling agent is additionally introduced into the forming solution of chitosan, wherein the coupling agent comprises glutaric aldehyde.
11. The method according to claim 5 , wherein a plastifying agent is additionally introduced into the forming solution of chitosan, wherein the plastifying agent comprises polyvinyl alcohol.
12. The method according to claim 1 , wherein a coupling agent is additionally introduced into the forming solution of hyaluronic acid, wherein the coupling agent comprises genipin.
13. The method according to claim 1 , wherein a coupling agent is additionally introduced into the forming solution of hyaluronic acid, wherein the coupling agent is selected from the group consisting of: ethyleneglycol diglycidyl ether, diethyleneglycol diglycidyl ether, triethyleneglycol diglycidyl ether, polyethyleneglycol diglycidyl ether, propyl eneglycol diglycidyl ether, 1,4-butanediol diglycidyl ether, and 1,6-hexandiol diglycidyl ether.
14. The method according to claim 1 , wherein a coupling agent is additionally introduced into the forming solution of hyaluronic acid, wherein the coupling agent comprises glutaric aldehyde.
15. The method according to claim 1 , wherein a plastifying agent is additionally introduced into the forming solution of hyaluronic acid, wherein the plastifying agent comprises polyvinyl alcohol.
16. A method for producing a multicomponent mesothread consisting of a core and a coating, wherein the core is a fibroin thread, comprising:
a. preparing a first forming solution of hyaluronic acid or its salt as follows:
i. swelling and dissolving of hyaluronic acid or its salt in water;
ii. adding to the obtained solution 10 to 40 mass % of ethyl alcohol with respect to weight of the obtained solution; and
iii. ripening and deaerating the obtained solution by ageing for 22±2 hours at the temperature of 22±2° C.;
b. preparing a second forming solution of chitosan or its salt as follows:
i. swelling and dissolving of chitosan or its salt in water;
ii. mixing the obtained solution gradually with an amount of concentrated acetic acid equal to the amount of chitosan;
iii. after the chitosan is dissolved, adding to the obtained solution 10 to 40 mass % of ethyl alcohol with respect to weight of the obtained solution; and
iv. ripening the obtained solution by ageing for 22±2 hours at the temperature of 22±2° C.;
c. in a first forming step:
i. drawing a fibroin thread through one of the first forming solution or the second forming solution;
ii. drawing the thread through a calibrated nozzle; and
iii. drying;
d. in a second forming step, following drying:
i. drawing the thread through one of the first forming solution or the second forming solution not used at the previous forming step;
ii. drawing the thread through a calibrated nozzle; and
iii. drying; and
e. repeating the second forming step until a mesothread of the desired thickness is completely formed, wherein the coating comprises a polyelectrolyte complex comprised of layers of hyaluronic acid or its salt alternating with layers of chitosan or its salt on the fibroin thread core.
17. The method according to claim 16 , wherein said hyaluronic acid salt comprises at least one of tetraalkylammonium, lithium, sodium, potassium, calcium, magnesium, barium, zinc, aluminum, copper, aurate, and hyaluronic acid hydrosalt.
18. The method according to claim 16 , wherein the chitosan comprises a chitosan with deacetylation degree over 50%, and the chitosan salt comprises chitosan acetate, chitosan chloride, or chitosan lactate.
19. The method according to claim 16 , wherein a coupling agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the coupling agent comprises genipin.
20. The method according to claim 16 , wherein a coupling agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the coupling agent is selected from the group consisting of: ethyleneglycol diglycidyl ether, diethyleneglycol diglycidyl ether, triethyleneglycol diglycidyl ether, polyethyleneglycol diglycidyl ether, propyleneglycol diglycidyl ether, 1,4-butanediol diglycidyl ether, and 1,6-hexandiol diglycidyl ether.
21. The method according to claim 16 , wherein a coupling agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the coupling agent comprises glutaric aldehyde.
22. The method according to claim 16 , wherein a plastifying agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the plastifying agent comprises polyvinyl alcohol.
23. The method according to claim 16 , wherein an antiinfection agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the antiinfection agent comprises beta-(5-nitrofuril-2)-acrolein.
24. The method according to claim 16 , wherein an antiseptic agent is additionally introduced into the first forming solution and/or the second forming solution, wherein the antiseptic agent comprises benzyldimethyl [3-(myristoylamino)propyl] ammonium chloride monohydrate.