Electroconductive support body and method for manufacturing same, electrophotographic photoreceptor, and electrophotographic device
An electrically conductive support for use in an electrophotographic photoreceptor includes a cylindrical main body having a first end and a second end opposite to the first end in an axial direction of the main body. The main body contains an aluminum alloy and has an internal stress in a range of −30 MPa to 5 MPa. A method of producing the electrically conductive support includes preparing a substrate containing an aluminum alloy obtained at least through an extrusion step, and heat treating the substrate to obtain the electrically conductive support. The heat treating is carried out such that, when a temperature of the heat treating is defined as T (° C.) and a time of the heat treating is defined as H (hours), an amount of the heat treating Q defined by Q=T×H is 800 or less.
1. An electrically conductive support for use in an electrophotographic photoreceptor, comprising:
a cylindrical main body having
a first end, and
a second end opposite to the first end in an axial direction of the main body,
wherein
the main body contains an aluminum alloy, and has an internal stress in a range of −30 MPa to 0 MPa.
2. The electrically conductive support according to claim 1 ,
wherein the main body is a cylindrical tube, and
wherein the cylindrical tube is a straight tube having the first end and the second end opposite to the first end in the longitudinal direction, the cylindrical tube having a constant inner outer diameter and a constant thickness an entire area between the first end and the second end.
3. The electrically conductive support according to claim 2 , wherein the cylindrical tube has the outer diameter of 40 mm or less, and the thickness in a range of 0.5 mm to 0.8 mm.
4. The electrically conductive support according to claim 2 , wherein the cylindrical tube has a deflection of 30 μm or less.
5. A method of producing the electrically conductive support according to claim 1 , comprising:
preparing a substrate obtained from an extrusion process, the substrate containing an aluminum alloy; and
heat treating the substrate to obtain the electrically conductive support, wherein
the heat treating is carried out such that, when a temperature of the heat treating is defined as T (° C.) and a time of the heat treating is defined as H (hours), an amount of the heat treating Q defined by Q=T×H is 800 or less.
6. An electrophotographic photoreceptor, comprising:
the electrically conductive support according to claim 1 ; and
a photosensitive layer disposed an outer surface of the main body.
7. The electrophotographic photoreceptor according to claim 6 , wherein the photosensitive layer contains an inorganic or organic filler.
8. The electrophotographic photoreceptor according to claim 6 , wherein the photosensitive layer contains at least a resin binder and a charge transport material.
9. An electrophotographic device comprising the electrophotographic photoreceptor according to claim 6 .