Modified polyvinyl alcohol and water-soluble film containing same
Modified polyvinyl alcohol contains a (meth)acrylamide monomer unit having an ionic group, wherein the modified polyvinyl alcohol has a degree of saponification of from 50 to 99.99 mol % and a viscosity-average degree of polymerization of from 200 to 5000 and satisfies formulae (1) to (3) below. The modified polyvinyl alcohol thus obtained is particularly excellent in dispersibility in water. 0.8≤( Mw UV /Mw RI )≤1.3 (1) 1≤( Mw UV /Mn UV )≤7 (2) 0.03≤ A 280 ≤0.5 (3).
1. A modified polyvinyl alcohol, comprising a (meth)acrylamide monomer unit having an ionic group, wherein the modified polyvinyl alcohol has a degree of saponification of from 50 to 99.99 mol % and a viscosity-average degree of polymerization of from 200 to 5000 and satisfies formulae (1) to (3):
0.8≤( Mw UV /Mw RI )≤1.3 (1)
1≤( Mw UV /Mn UV )≤7 (2)
0.03≤ A 280 ≤0.5 (3),
Mw UV : weight-average molecular weight of the modified polyvinyl alcohol measured by an absorptiometer (measurement wavelength of 280 nm) in gel permeation chromatographic measurement of the modified polyvinyl alcohol after heating at 120° C. for 3 hours,
Mw RI : weight-average molecular weight of the modified polyvinyl alcohol measured by a differential refractive index detector in gel permeation chromatographic measurement of the modified polyvinyl alcohol after heating at 120° C. for 3 hours,
Mn UV : number-average molecular weight of the modified polyvinyl alcohol measured by an absorptiometer (measurement wavelength of 280 nm) in gel permeation chromatographic measurement of the modified polyvinyl alcohol after heating at 120° C. for 3 hours,
A 280 : absorbance (optical path length of 10 mm, measurement wavelength of 280 nm) of a 1 mass % aqueous solution of the modified polyvinyl alcohol after heating at 120° C. for 3 hours.
2. The modified polyvinyl alcohol according to claim 1 , wherein a content of the monomer unit is from 0.1 to 10 mol %.
3. The modified polyvinyl alcohol according to claim 1 , wherein the ionic group is a group comprising a sulfonic acid or a salt thereof.
4. The modified polyvinyl alcohol according to claim 1 , wherein the ionic group is a group comprising an amine, an amine salt, or a quaternary ammonium salt.
5. A water-soluble film, comprising the modified polyvinyl alcohol according to claim 1 .
6. A package, comprising the water-soluble film according to claim 5 , and a chemical contained in the water-soluble film.
7. The package according to claim 6 , wherein the chemical is an agrochemical or a detergent.