Optical fiber
The optical fiber offered is capable of not only restraining the attenuation due to glass defects, but also reducing the increase of manufacturing cost. The optical fiber is made of silica glass and includes a core and a cladding. The cladding encloses the core and has a refractive index smaller than that of the core. When the core is divided into inner core and outer core at half of the radius of the core, the average chlorine concentration of the inner core is larger than that of the outer core. The core includes any of the alkali metal group.
1. An optical fiber made of silica glass and comprising:
a core containing an alkali metal or an alkaline-earth-metal element and having a radius of r 0 ; and
a cladding enclosing the core and having a refractive index smaller than that of the core,
wherein the core includes an inner core having a radius of r 0 /2 and an outer core having an inside radius of r 0 /2 and an outside radius of r 0 , and the average chlorine concentration of the inner core is larger than that of the outer core, and;
the rate A/B of the average chlorine concentration A of the inner core to the average chlorine concentration B of the outer core is larger than 1.5.
2. An optical fiber as set forth in claim 1 ,
wherein the rate of change of chlorine concentration in the radial direction of the core is not more than 10 ppm by mass per 1 μm.
3. An optical fiber as set forth in claim 1 ,
wherein the average Chlorine concentration of the inner core is from 100 ppm by mass to 2000 ppm by mass.
4. An optical fiber as set forth in claim 1 ,
wherein the average chlorine concentration of the outer core is from 100 ppm by mass to 2000 ppm by mass.
5. An optical fiber as set forth in claim 1 ,
wherein the ratio A/B of the average chlorine concentration A of the inner core to the average chlorine concentration B of the outer core is larger than 2.0.
6. An optical fiber as set forth in claim 1 ,
Wherein the core contains fluorine.
7. An optical fiber as set forth in claim 6 ,
wherein the average fluorine concentration in the core is 500 to 5000 ppm by mass.
8. An optical fiber as set forth in claim 1 ,
wherein the average concentration of the alkali metal group in the core is 0.2 to 200 ppm by mass.
9. An optical fiber as set forth in claim 1 ,
wherein the core contains one or more elements selected from a group consisting of sodium, potassium, rubidium, cesium, and calcium.
10. An optical fiber as set forth in claim 1 ,
wherein the number of propagation mode at the wavelength of 1550 nm is one.
11. An optical fiber as set forth in claim 1 ,
wherein the number of propagation mode at the wavelength of 1550 nm is two or more.
12. An optical fiber made of silica glass and comprising:
a core containing an alkali metal or an alkaline-earth-metal element and having a radius of r 0 ; and
a cladding enclosing the core and having a refractive index smaller than that of the core,
wherein the core includes an inner core having a radius of r 0 /2 and an outer core having an inside radius of r 0 /2 and an outside radius of r 0 , and the average chlorine concentration of the inner core is larger than that of the outer core, and
wherein the core contains fluorine and the average fluorine concentration in the core is 500 to 5000 ppm by mass.
13. An optical fiber as set forth in claim 12 ,
wherein the rate of change of chlorine concentration in the radial direction of the core is not more than −10 ppm by mass per 1 μm.
14. An optical fiber as set forth in claim 12 ,
wherein the average chlorine concentration of the inner core is from 100 ppm by mass to 2000 ppm by mass.
15. An optical fiber as set forth in claim 12 ,
wherein the average chlorine concentration of the outer core is from 100 ppm by mass to 2000 ppm by mass.
16. An optical fiber as set forth in claim 12 ,
wherein the average concentration of the alkali metal group in the core is 0.2 to 200 ppm by mass.
17. An optical fiber as set forth in claim 12 ,
wherein the core contains one or more elements selected from a group consisting of sodium, potassium, rubidium, cesium, and calcium.
18. An optical fiber made of silica glass and comprising:
a core containing an alkali metal or an alkaline-earth-metal element and having a radius of r 0 ; and
a cladding enclosing the core and having a refractive index smaller than that of the core,
wherein the core includes an inner core having a radius of r 0 /2 and an outer core having an inside radius of r 0 /2 acid an outside radius of r 0 , and the average chlorine concentration of the inner core is larger than that of the outer core, and
wherein the average concentration of the alkali metal group in the core is 0.2 to 200 ppm by mass.
19. An optical fiber as set forth in claim 18 ,
wherein the rate of change of chlorine concentration in the radial direction of the core is of more than −10 ppm by mass per 1 μm.
20. An optical fiber as set forth in claim 18 ,
wherein the average chlorine concentration of the inner core is from 100 ppm mass to 2000 ppm by mass.
21. An optical fiber as set forth in claim 18 ,
wherein the average chlorine concentration of the outer core is from 100 ppm by mass to 2000 ppm by mass.
22. An optical fiber as set forth in claim 18 ,
wherein the core contains one or more elements selected from a group consisting of sodium, potassium, rubidium, cesium, and calcium.