Supercritical CO2 cellulose spraydrying
The present invention provides for a process for producing dry, water-dispersible, non-surface modified nanocellulose particles or a powderous composition r comprising said particles comprising the steps of: i. providing a first suspension of non-surface modified cellulose particles in an first aqueous liquid, which aqueous liquid is non-solubilizing for the non-surface modified nanocellulose particles, ii. exchanging substantially all of the first aqueous liquid of the first suspension for a second solvent, which is miscible with the first aqueous liquid and non-solubilizing for the non-surface modified nanocellulose particles, to form a second suspension of non-surface modified nanocellulose particles in said second solvent, iii. contacting a flow of the second suspension of non-surface modified nanocellulose particles with a flow of a fluid in a supercritical or critical state, which fluid in a supercritical or critical state is miscible with the second solvent and non-solvating for the non-surface modified nanocellulose particles under conditions suitable for the transfer of substantially all of the second solvent into the supercritical fluid, iv. removing the second solvent and the fluid in a supercritical or critical state, preferably by controlling pressure and/or temperature, to form the dry, water-dispersible nanocellulose particles, v. collecting the dry, water-dispersible, non-surface modified nanocellulose particles and/or forming the powderous composition comprising said particles.
1. A process for producing dry, water dispersible, non-surface modified nanocellulose particles or a powderous composition comprising said particles comprising the steps of:
i. providing a first suspension of non-surface modified cellulose particles in a first aqueous liquid, wherein the first aqueous liquid is non-solubilising for the non-surface modified cellulose particles and processing the first suspension of non-surface modified cellulose particles in the first aqueous liquid to form a first suspension of non-surface modified nanocellulose articles in the first aqueous liquid,
ii. exchanging the first aqueous liquid of the first suspension of non-surface modified nanocellulose particles for a second solvent which is miscible with the first aqueous liquid of the first suspension of non-surface modified nanocellulose particles and non-solubilising for the non-surface modified nanocellulose particles to form a second suspension of non-surface modified nanocellulose particles in said second solvent,
iii. contacting a flow of the second suspension of non-surface modified nanocellulose particles with a flow of a fluid in a supercritical or critical slate, wherein the fluid in a supercritical or critical state is miscible with the second solvent and non-solvating for the non-surface modified nanocellulose particles under conditions suitable for the transfer of the second solvent into the supercritical fluid,
iv. removing the second solvent and the fluid in a supercritical or critical state to form the dry, water dispersible, non-surface modified nanocellulose particles, and
v. collecting the dry, water dispersible, non-surface modified nanocellulose particles and/or forming a powderous composition comprising said particles.
2. The process according to claim 1 , wherein the first aqueous liquid is either water or a mixture of water and one or more organic solvents capable of acting as swelling agents.
3. The process according to claim 1 , wherein the first suspension of non-surface modified cellulose particles comprises up to 20 wt % of the non-surface modified cellulose particles.
4. The process according to claim 1 , wherein in the step of contacting the flow of the second suspension of non-surface modified nanocellulose particles with the flow of the fluid in a supercritical or critical state, the mass flow ratio between the second suspension and the fluid in a supercritical or critical state is in the range of 1:10000 to 3:10.
5. The process according to claim 1 , wherein in step iii, the second suspension and the fluid in a supercritical or critical state are contacted either;
vi. by simultaneously atomizing the flow of the second suspension of non-surface modified nanocellulose particles and the flow of the fluid in a supercritical or critical state separately through one or more nozzles into a pressure-controlled and/or temperature-controlled particle formation vessel, or
vii. by blending, swirling, vortexing or mixing the flow of the second suspension and the flow of the fluid in a supercritical or critical state to form a mixture and atomizing said mixture through one or more nozzles into a pressure controlled- and/or temperature-controlled particle formation vessel.
6. The process according to claim 1 , wherein in step the second suspension and the fluid in a supercritical or critical state are contacted by simultaneously atomizing the flow of the second suspension of non-surface modified nanocellulose particles and the flow of the fluid in a supercritical or critical state separately through one or more concentric or coaxial nozzles into a pressure-controlled and/or temperature-controlled particle formation vessel, the second suspension being flowed through a central jet of the concentric or coaxial nozzle and the fluid in a supercritical or critical state being flowed through an annular peripheral jet of the concentric or coaxial nozzle.
7. The process according to claim 1 , wherein the second solvent is chosen from organic solvents.
8. The process according to claim 1 , wherein the fluid in a supercritical or critical state is a fluid comprising carbon dioxide.
9. The process according to claim 1 , wherein in step iv., the second solvent and the fluid in a supercritical or critical state are removed by controlling pressure and/or temperature.
10. The process according to claim 1 , wherein the first aqueous liquid is a mixture of water and a cyclic secondary amine comprising of from 60 to 99% by volume of cyclic amine.
11. The process according to claim 1 , wherein the first aqueous liquid is a mixture of water and morpholine, piperidine or both.
12. The process according to claim 1 , wherein the first aqueous liquid is a mixture of water and morpholine, piperidine or both comprising of from 60 to 99% by volume of morpholine, piperidine or both.
13. The process according to claim 1 , wherein the first aqueous liquid is a mixture of water and morpholine, piperidine or both comprising of from 70 to 95% by volume of morpholine or piperidine or both.
14. The process according to claim 1 , wherein the first suspension of non-surface modified cellulose particles comprises from 0.1 to 20 wt % of the non-surface modified cellulose particles.
15. The process according to claim 1 , wherein the first suspension of non-surface modified cellulose particles comprises more than 2 wt % and less than 20 wt % of the non-surface modified cellulose particles.
16. The process according to claim 1 , wherein in the step of contacting the flow of the second suspension of non-surface modified nanocellulose particles with the flow of the fluid in a supercritical or critical state, the mass flow ratio between the second suspension and the fluid in a supercritical or critical state is in the range of 3:10000 to 3:10.
17. The process according to claim 1 , wherein the second solvent is chosen from polar solvents chosen from alcohols, aldehydes, or ketones.
18. The process according to claim 1 , wherein the second solvent is chosen from chosen from C1-C4 alcohols or from C1-C4 ketones.
19. The process according to claim 1 , wherein the second solvent is chosen from ethanol, isopropanol or acetone.
20. The process according to claim 1 , wherein the fluid in a supercritical or critical state is carbon dioxide.