Aluminum alloy brazing sheet
An aluminum alloy brazing sheet used for brazing aluminum, without using a flux, in an inert gas atmosphere or vacuum is formed by arranging a brazing material on one side or both sides of a core material made of pure aluminum or aluminum alloy, the brazing material including 6% to 13% by mass of Si and the balance being Al and inevitable impurities, and performing cladding with an intermediate material interposed between the core material and the brazing material, the intermediate material including 0.01% to 1.5% by mass of Bi, 1.5% to 13% by mass of Si, and the balance being Al and inevitable impurities, the intermediate material having a thickness of 2% to 35% of a thickness of the brazing material, wherein one or both of the intermediate material and the core material includes 0.4% to 6% by mass of Mg.
1. An aluminum alloy brazing sheet used for brazing aluminum including aluminum alloy, without using a flux, in an inert gas atmosphere or vacuum, the brazing sheet being formed by arranging a brazing material on one side or both sides of a core material made of pure aluminum or aluminum alloy, the brazing material including 6% to 13% by mass of Si and the balance being Al and inevitable impurities, and performing cladding with an intermediate material interposed between the core material and the brazing material, the intermediate material including 0.01% to 1.5% by mass of Bi, 1.5% to 13% by mass of Si, and the balance being Al and inevitable impurities, the intermediate material having a thickness of 2% to 35% of a thickness of the brazing material, wherein
one or both of the intermediate material and the core material includes 0.4% to 6% by mass of Mg.
2. The aluminum alloy brazing sheet according to claim 1 , wherein the core material made of aluminum alloy includes at least one of 1.8% by mass or less of Mn, 1.2% by mass or less of Si, 1.0% by mass or less of Fe, 1.5% by mass or less of Cu, 0.8% by mass or less of Zn, 0.2% by mass or less of Ti, and 0.5% by mass or less of Zr, and the balance being Al and inevitable impurities.
3. The aluminum alloy brazing sheet according to according to claim 1 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.
4. The aluminum alloy brazing sheet according to according to claim 2 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.
5. An aluminum alloy brazing sheet used for brazing aluminum including aluminum alloy, without using a flux, in an inert gas atmosphere or vacuum, the brazing sheet being formed by arranging a brazing material on one side or both sides of a core material made of pure aluminum or aluminum alloy, the brazing material including 6% to 13% by mass of Si and the balance being Al and inevitable impurities, and performing cladding with an intermediate material and a sacrificial anode material interposed between the core material and the brazing material such that the materials are arranged in an order of the core material, the sacrificial anode material, the intermediate material, and the brazing material, the intermediate material including 0.01% to 1.5% by mass of Bi, 1.5% to 13% by mass of Si, and the balance being Al and inevitable impurities, the sacrificial anode material including 0.9% to 6% by mass of Zn and the balance being Al and inevitable impurities, the intermediate material having a thickness of 2% to 35% of a thickness of the brazing material, wherein
at least one of the intermediate material, the sacrificial anode material, and the core material includes 0.4% to 6% by mass of Mg.
6. The aluminum alloy brazing sheet according to claim 5 , wherein the core material made of aluminum alloy includes at least one of 1.8% by mass or less of Mn, 1.2% by mass or less of Si, 1.0% by mass or less of Fe, 1.5% by mass or less of Cu, 0.8% by mass or less of Zn, 0.2% by mass or less of Ti, and 0.5% by mass or less of Zr, and the balance being Al and inevitable impurities.
7. The aluminum alloy brazing sheet according to according to claim 5 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.
8. The aluminum alloy brazing sheet according to according to claim 6 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.
9. An aluminum alloy brazing sheet used for brazing aluminum including aluminum alloy, without using a flux, in an inert gas atmosphere or vacuum, the brazing sheet being formed by arranging a brazing material on one side of a core material made of pure aluminum or aluminum alloy, the brazing material including 6% to 13% by mass of Si and the balance being Al and inevitable impurities, arranging a sacrificial anode material on the other side of the core material, the sacrificial anode material including 0.9% to 6% by mass of Zn and the balance being Al and inevitable impurities, and performing cladding with an intermediate material interposed between the core material and the brazing material, the intermediate material including 0.01% to 1.5% by mass of Bi, 1.5% to 13% by mass of Si, and the balance being Al and inevitable impurities, the intermediate material having a thickness of 2% to 35% of a thickness of the brazing material, wherein
one or both of the intermediate material and the core material includes 0.4% to 6% by mass of Mg.
10. The aluminum alloy brazing sheet according to claim 9 , wherein the core material made of aluminum alloy includes at least one of 1.8% by mass or less of Mn, 1.2% by mass or less of Si, 1.0% by mass or less of Fe, 1.5% by mass or less of Cu, 0.8% by mass or less of Zn, 0.2% by mass or less of Ti, and 0.5% by mass or less of Zr, and the balance being Al and inevitable impurities.
11. The aluminum alloy brazing sheet according to according to claim 9 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.
12. The aluminum alloy brazing sheet according to according to claim 10 , wherein the intermediate material further includes one or two of 6% by mass or less of Cu and 6% by mass or less of Zn.