Basalt processing via electric induction heating and melting
An electric induction system and method is provided for induction heating and melting of basalt charge for the production of molten process basalt that can be used for molten basalt processes that produce basalt articles of manufacture including cast basalt articles and continuous basalt casting processes for producing basalt articles such as fibers and filaments.
1. A method of melting and heating a basalt charge with electric induction to supply a molten process at a molten process basalt temperature for a basalt article manufacturing process, the method comprising:
inductively heating the basalt charge in a high temperature cold crucible induction furnace via a first alternating current power supplied at 600 kW and a high temperature frequency in a range of 300 kHz to 600 kHz to a high temperature induction coil surrounding an exterior height of the high temperature cold crucible induction furnace to form a heated molten basalt batch in a temperature range of 1500° C. to 2000° C. in the high temperature cold crucible induction furnace;
continuously gravity flowing the heated molten basalt batch from the high temperature cold crucible induction furnace to a molten process basalt cold crucible induction furnace while controlling a time rate of adding the basalt charge to the high temperature cold crucible induction furnace and the first alternating current power; and
inductively heating the heated molten basalt batch in the molten process basalt cold crucible induction furnace via a second alternating current power supplied in a range of 150 kW to 300 kW at a molten process basalt frequency in a range of 300 kHz to 800 kHz to a molten process basalt induction coil surrounding an exterior height of the molten process basalt cold crucible induction furnace to form a molten process basalt in a temperature range of 1400° C. to 1500° C. in the molten process basalt cold crucible induction furnace.
2. The method of claim 1 further comprising casting the molten process basalt through a casting plenum at a bottom of the molten process basalt cold crucible induction furnace to form a basalt filament or a basalt fiber.
3. The method of claim 1 further comprising electromagnetically stirring the heated molten basalt batch or the molten process basalt.
4. A method of melting and heating a basalt charge with electric induction to supply a molten process at a molten process basalt temperature for a basalt article manufacturing process, the method comprising:
inductively heating the basalt charge in a high temperature cold crucible induction furnace via a first alternating current power supplied at 600 kW and a high temperature frequency in a range of 300 kHz to 600 kHz to a high temperature induction coil surrounding an exterior height of the high temperature cold crucible induction furnace to form a heated molten basalt batch in a temperature range of 1500° C. to 2000° C. in the high temperature cold crucible induction furnace;
continuously supplying the heated molten basalt batch from the high temperature cold crucible induction furnace to a molten process basalt cold crucible induction furnace via an enclosed cold crucible launder having an interior launder passage connecting an interiors of the high temperature cold crucible induction furnace and the molten process basalt cold crucible induction furnace; and
inductively heating the heated molten basalt batch in the molten process basalt cold crucible induction furnace via a second alternating current power supplied in the range of 150 kW to 300 kW at a molten process basalt frequency in a range of 300 kHz to 800 kHz to a molten process basalt induction coil surrounding an exterior height of the molten process basalt cold crucible induction furnace to form a molten process basalt in the range of 1500° C. to 2000° C. in the molten process basalt cold crucible induction furnace.
5. The method of claim 4 further comprising controlling a launder temperature of the heated molten basalt batch in the enclosed cold crucible launder by flowing a fluid cooling medium through an interior passage in each of a plurality of segmented wall sections of the enclosed cold crucible launder.
6. The method of claim 4 further comprising casting the molten process basalt through a casting plenum at a bottom of the molten process basalt cold crucible induction furnace to form a basalt filament or a basalt fiber.
7. The method of claim 4 further comprising electromagnetically stirring the heated molten basalt batch or the molten process basalt.