Activator composition and method for making concrete
An activator composition for a non-OPC hydraulically-active material comprises CaO or lime and a polycarboxylate-ether-based (PCE) superplasticiser, and is mixable with a hydraulically active material comprising ground granulated blast furnace slag (GGBS) and/or pulverized fuel ash (PFA) to form a cementitious binder. The cementitious binder does not comprise any Portland cement and is, therefore, more environmentally friendly.
1. An activator composition mixable with a non-OPC hydraulically-active material comprising ground granulated blast furnace slag (GGBS), the activator composition comprising an activator, which is CaO or lime, and a polycarboxylate-ether-based (PCE) superplasticizer, and a further component which is microsilica and/or pulverised fuel ash (PFA).
2. An activator composition according to claim 1 , in which the activator and the PCE superplasticiser are mixed in a weight ratio of between 1:1 and 38:1.
3. An activator composition according to claim 1 , in which the activator and the further component are mixed in a weight ratio of between 1.2:1 and 3:1.
4. An activator composition according to claim 1 , in which the PCE superplasticiser is in powder form.
5. An activator composition according to claim 1 , in which the activator and the PCE superplasticiser are mixed in a weight ratio of between 1:1 and 6:1.
6. An activator composition according to claim 1 , in which the activator composition is in powdered form.
7. An activator composition according to claim 1 , in which the activator composition is pre-blended.
8. An activator composition mixable with a non-OPC hydraulically-active material comprising ground granulated blast furnace slag (GGBS), pulverised fuel ash (PFA) or a mixture of GGBS and PFA, the activator composition comprising an activator, which is CaO or lime, and a polycarboxylate-ether-based (PCE) superplasticizer, and in which the activator composition is contained within one or more water-soluble packages and is releasable from the one or more water-soluble packages on contact with water.
9. An activator composition according to claim 1 , An activator composition mixable with a non-OPC hydraulically-active material comprising ground granulated blast furnace slag (GGBS), pulverised fuel ash (PFA) or a mixture of GGBS and PFA, the activator composition comprising an activator, which is CaO or lime, and a polycarboxylate-ether-based (PCE) superplasticizer, and in which the activator composition is packaged in a package for use in mixing with a hydraulically-active material, the package releasing the activator composition on contact with water.
10. An activator composition for combining with a hydraulically-active material comprising ground granulated blast furnace slag (GGBS), the activator composition comprising a first component consisting of CaO or lime and a second component consisting of a PCE superplasticizer, and a third component consisting of microsilica, PFA, or a mixture of microsilica and PFA.
11. An activator composition according to claim 10 , in which the activator and the superplasticiser are mixed in a weight ratio of between 1:1 and 38:1.
12. An activator composition according to claim 10 , in which the superplasticiser is in powder form.
13. An activator composition according to claim 10 , in which the activator and the further component are mixed in a weight ratio of between 1.2:1 and 3:1.
14. An activator composition according to claim 10 , in which a quantity of the activator composition is packaged in a package for use in mixing with a hydraulically-active material, the package releasing the activator composition on contact with water.
15. An activator composition according to claim 10 , in which the activator and the superplasticiser are mixed in a weight ratio of between 1:1 and 6:1.