Salt-resistant hydrophobically modified copolymer nanostructures as viscosity increasing agents for enhanced oil recovery
A hydrophobically modified copolymer nanostructure includes a first monomer and a second monomer. The first monomer is a hydrophilic monomer. The second monomer is a non-ionic short-chain hydrophobic monomer. The first monomer and the second monomer form a microblock structure, forming nanoparticles. The microblock structure is the hydrophobically modified copolymer nanostructure.
1. A method of producing a hydrophobically modified copolymer nanostructure, the method comprising;
adding a hydrophilic monomer, an osmotic agent and a surfactant to an organic solvent to produce a nano-emulsion;
adding a hydrophobic monomer to the produced nano-emulsion and an oil-soluble initiator to start a reaction and produce the hydrophobically modified copolymer; and
recovering the hydrophobically modified copolymer nanostructure from the organic solvent.
2. The method of claim 1 , wherein producing the nano-emulsion includes adding the hydrophilic monomer, osmotic agent and the surfactant to the organic solvent and stirring the mixture.
3. The method of claim 2 , wherein the osmotic agent includes a sodium hydroxide solution.
4. The method of claim 2 , wherein the surfactant includes a surfactant with HLB of 2-6.
5. The method of claim 2 , wherein:
the organic solvent includes cyclohexane, benzene or heptane.
6. The method of claim 2 , wherein:
the initiator includes an oil-soluble initiator, and
the oil-soluble initiator includes azobisisobutyronitrile (AIBN), benzoyl peroxide (BPO) or lauroyl peroxide (LPO).
7. The method of claim 2 , wherein:
the osmotic agent includes a sodium hydroxide solution,
the organic solvent includes cyclohexane, benzene or heptane,
the initiator includes an oil-soluble initiator, and
the oil-soluble initiator includes benzoyl peroxide (BPO), lauroyl peroxide (LPO) or azobisisobutyronitrile (AIBN).
8. The method of claim 1 , further comprising polymerizing the hydrophobic monomer, wherein the polymerizing includes adding the hydrophobic monomer to the nano-emulsion while under mechanical stirring, to form micelles, and then adding the initiator of the reaction to synthesize the hydrophobically modified copolymer nanostructure as a hydrophobic/hydrophilic polymer.
9. The method of claim 8 , wherein producing the nano-emulsion includes adding the hydrophilic monomer, the osmotic agent and the surfactant to the organic solvent and stirring the mixture.
10. The method of claim 9 , wherein:
the osmotic agent includes a sodium hydroxide solution,
the organic solvent includes cyclohexane, benzene or heptane,
the initiator includes benzoyl peroxide (BPO), lauroyl peroxide (LPO) or azobisisobutyronitrile (AIBN).
11. The method of claim 1 , wherein polymerizing leaves unreacted monomers and unreacted surfactant, and wherein recovering the hydrophobically modified copolymer nanostructure comprises rinsing the hydrophobically modified copolymer nanostructure by methanol to separate unreacted monomers and unreacted surfactant from the hydrophobically modified copolymer nanostructure.
12. The method of claim 11 , wherein recovering the hydrophobically modified copolymer nanostructure further comprises drying the hydrophobically modified copolymer nanostructure under vacuum.