Heat-conductive silicone grease composition
A heat-conductive silicone grease composition comprising (A) an organopolysiloxane in an amount of 20 to 90 parts by mass, (B) a non-silicone-type organic compound in an amount of 80 to 10 parts by mass (wherein the total amount of the components (A) and (B) is 100 parts by mass) and (C) a heat-conductive inorganic filler having an average particle diameter of 0.5 to 100 μm in an amount of 200 to 2,000 parts by mass relative to 100 parts by mass of the total amount of the components (A) and (B), wherein the SP value of the non-silicone-type organic compound (B) is greater than that of the organopolysiloxane (A) (i.e., (B)>(A)), the value obtained by subtracting the SP value of the component (A) from the SP value of the component (B) is greater than 2, and the viscosity of the heat-conductive silicone grease composition is 50 to 1,000 Pa·s at 25° C.
1. A thermally conductive silicone grease composition comprising
(A) from 20 to 90 parts by weight of an organopolysiloxane,
(B) from 80 to 10 parts by weight of a non-silicone organic compound which is an aromatic liquid compound with a functionality of 3 or less that has on the molecule an organic group selected from among epoxy, phenolic hydroxyl and amino groups, the combined amount of components (A) and (B) being 100 parts by weight, and
(C) a thermally conductive inorganic filler having an average particle size of from 0.5 to 100 μm, in an amount of from 200 to 2,000 parts by weight per 100 parts by weight of components (A) and (B) combined,
wherein the non-silicone organic compound (B) and the organopolysiloxane (A) have respective solubility parameters (SP) such that
the SP of component (B) >the SP of component (A), and
the SP of component (B)−the SP of component (A) >2; and
the thermally conductive silicone grease composition has a viscosity at 25° C. of from 50 to 1,000 Pa·s.
2. The thermally conductive silicone grease composition of claim 1 , wherein the organopolysiloxane (A) is a hydrolyzable organopolysiloxane of general formula (1) below which has a viscosity at 25° C. of from 0.005 to 100 mPa·s
wherein each R 1 is a like or unlike monovalent hydrocarbon group, each X is R 1 or a group of the formula —R 2 —SiR 1 (3-a) (OR 3 ) a wherein R 1 being as defined above; R 2 being an oxygen atom or an alkylene group of 1 to 4 carbon atoms; R 3 being an alkyl, alkoxyalkyl, alkenyl or acyl group of 1 to 4 carbon atoms; and the letter “a” being an integer from 1 to 3, and m and n respectively satisfy the conditions 1≤m≤1,000 and 0≤n≤1,000;
the non-silicone organic compound (B) is a compound with a solubility parameter of 10 or more which has on the molecule an organic group selected from among epoxy, phenolic hydroxyl and amino groups; and
the thermally conductive inorganic filler (C) is of at least one selected from the group consisting of metallic powders, metal oxide powders, metal hydroxide powders and metal nitride powders.
3. The thermally conductive silicone grease composition of claim 2 , wherein the organopolysiloxane (A) is a hydrolyzable organopolysiloxane having three or six OR 3 groups (wherein R 3 is as defined above).
4. The thermally conductive silicone grease composition of claim 2 , wherein the non-silicone organic compound (B) is an aromatic liquid epoxy resin having a functionality of 3 or less.
5. The thermally conductive silicone grease composition of claim 1 , wherein the thermally conductive inorganic filler (C) is one or a combination of two or more selected from the group consisting of aluminum, silver, copper, nickel, zinc oxide, aluminum oxide, silicon oxide, magnesium oxide, aluminum nitride, boron nitride, silicon nitride and metallic silicon.
6. The thermally conductive silicone grease composition of claim 1 , wherein the non silicone organic compound (B) is selected from the group consisting of bisphenol A type liquid epoxy resins, bisphenol F type liquid epoxy resins, 4-(2,3-epoxypropoxy)-N,N-glycidylaniline, N,N-diglycidylaniline, N,N-diglycidyltoluidine, 4,4′-diamino-3,3′-dimethyldiphenylmethane, and 4,4′-dihydroxy-3,3′-diallyldiphenylmethane.