Olefin polymer and method for preparing same
The present invention provides an olefin polymer in which LCB (long chain branch) is introduced into mLLDPE (metallocene linear low-density polyethylene) to control the storage modulus, whereby the olefin polymer has excellent bubble stability and processing load characteristics and exhibits excellent processability during preparation of a film, and further has excellent mechanical properties and transparency.
1. An olefin polymer having a haze parameter of 11 or less which is determined according to the following Equation 1:
Haze parameter=0.0036× G′+ 6.25+400×( D− 0.920) [Equation 1]
in the above Equation 1,
D is a density of the olefin polymer measured according to ASTM D792, and
G′ is a storage modulus measured at 5% strain and 0.05 rad/s in the dynamic strain sweep frequency mode using an ARES rheometer.
2. The olefin polymer of claim 1 , wherein the G′ is 1500 dyn/cm 2 or less.
3. The olefin polymer of claim 1 , wherein the D is 0.910 g/cm 3 to 0.930 g/cm 3 .
4. The olefin polymer of claim 1 , wherein it has a strength factor of 50 or more which is determined according to the following Equation 2:
Strength Factor ( SF )= Mw/ 10 4 +5/( Mw/ 10 5 )×exp(ratio of increase in elongational viscosity) [Equation 2]
in the above Equation 2, Mw means a weight average molecular weight,
the ratio of increase in elongational viscosity is a value in which the highest elongational viscosity value measured for the olefin polymer at Hencky strain rate of 1 s −1 at 170° C. using an extensional viscosity fixture attached to the ARES rheometer is divided by the elongational viscosity value of the extrapolated straight line at the time when the highest elongational viscosity value is obtained, wherein the extrapolated straight line is a straight line in which a straight line having the average slope of the section where the elongational viscosity increases steadily with time is extended to a section where the elongational viscosity increases sharply while maintaining the above average slope.
5. The olefin polymer of claim 4 , wherein the ratio of increase in elongational viscosity is 2.0 or more.
6. The olefin polymer of claim 1 , wherein it has a melt index of 0.3 g/10 min or more and less than 4 g/10 min, which is measured at a temperature of 190° C. under a load of 2.16 kg according to standard ASTM D 1238.
7. The olefin polymer of claim 1 , wherein it has a number average molecular weight of 20,000 g/mol to 60,000 g/mol, and a weight average molecular weight of 90,000 g/mol to 160.000 g/mol.
8. The olefin polymer of claim 1 , wherein it has MFRR (21.6/2.16) of 18 or more and less than 40 in which a melt flow rate (MFR 21.6 ) measured at a temperature of 190° C. under a load of 21.6 kg according to ISO 1133 is divided by a melt flow rate (MFR 2.16 ) measured at a temperature of 190° C. under a load of 2.16 kg according to ISO 1133.
9. The olefin polymer of claim 1 , wherein it has melt strength of 50 mN to 100 mN.
10. The olefin polymer of claim 1 , which is a copolymer of ethylene and alpha olefin.
11. The olefin polymer of claim 1 , which is a copolymer of ethylene and 1-hexene.
12. A blown film, comprising the olefin polymer of claim 1 , wherein the film has a haze of 10% or less as measured according to ISO 14782.