UV curable ink for inkjet, method for manufacturing a bezel using the same, a bezel pattern using the same method and display panel comprising the bezel pattern

1. A method of manufacturing a bezel using UV-curable inkjet ink, comprising:

a) subjecting a substrate to inkjet printing using UV-curable inkjet ink, thus forming a substrate having a bezel, wherein the UV-curable inkjet ink is a UV curable ink composition having a black color, a viscosity of from 1 cP to 20 cP, and includes 10 wt % to 40 wt % of a carbon black pigment, based on the total weight of the UV-curable inkjet ink;

b) thermally treating the substrate having the bezel in an oven at a temperature of 90 to 110° C. for 120 to 180 sec. or on a hot plate at a temperature of 100 to 120° C. for 5 to 10 min., thus eliminating cure shrinkage; and

c) irradiating the bezel with UV light, thus forming a cured bezel,

wherein the cured bezel in c) has a surface hardness of 4H or more and an adhesion of 5B,

wherein the cured bezel in c) is non-conductive and has a light-shielding property, and

wherein the cured bezel in c) has an optical density of 4 to 6.

2. The method of claim 1 , wherein the cured bezel in c) has a thickness of 2 to 6 μm.

3. The method of claim 1 , wherein the UV curable ink composition further comprises an adhesion promoter, a binder solution, a multifunctional monomer, and a photoinitiator.

4. The method of claim 3 , wherein the adhesion promoter is a monomer selected from the group consisting of 2-hydroxyethyl acrylate (2-HEA), hydroxypropyl acrylate (HPA), 2-hydroxyethyl methacrylate (2-HEMA), and hydroxypropyl methacrylate (HPMA).

5. The method of claim 3 , wherein the adhesion promoter is 2-hydroxyethyl acrylate (2-HEA).

6. The method of claim 3 , wherein the adhesion promoter is present in an amount of from 5 wt % to 25 wt % based on the total weight of the ink composition.

7. The method of claim 3 , wherein the binder solution is present in an amount of from 5 wt % to 20 wt % based on the total weight of the ink composition.

8. The method of claim 3 , wherein the binder solution comprises an epoxy resin and a second reactive monomer.

9. The method of claim 8 , wherein the second reactive monomer is selected from the group consisting of hydroxyethyl acrylate (HEA), hydroxyethyl methacrylate (HEMA), hexanediol diacrylate (HDDA), neopentylglycol hydroxypivalate (HPNDA), tripropyleneglycol diacrylate (TPGDA), and mixtures thereof.

10. The method of claim 8 , wherein the epoxy resin to the second reactive monomer are present at a weight ratio of from 20:80 to 30:70, based on the total weight of the ink composition.

11. The method of claim 3 , wherein the multifunctional monomer is present in an amount of from 1 wt % to 20 wt % based on the total weight of the ink composition.

12. The method of claim 3 , wherein the photoinitiator is present in an amount of from 0.1 wt % to 10 wt % based on the total weight of the ink composition.

13. The method of claim 1 , wherein the UV-curable inkjet ink composition has a cure dose of 1 mJ/cm 2 to 10,000 mJ/cm 2 .

14. The method of claim 1 , wherein the UV-curable inkjet ink composition absorbs UV light at a wavelength ranging from 360 nm to 410 nm.

15. The method of claim 1 , wherein the UV-curable inkjet ink composition comprises from 50 wt % to 65 wt % of a pigment dispersion.

16. The method of claim 15 , wherein the pigment dispersion comprises carbon black, a dispersant, and a first reactive monomer.

17. The method of claim 16 , wherein the first reactive monomer is 1,6-hexanediol diacrylate, neopentylglycol hydroxypivalate (HPNDA), trimethylolpropane triacrylate (TMPTA), pentaerythritol triacrylate, trimethylenepropane triacrylate, propoxylated glycerol triacrylate, or a mixture thereof.