Two-dimensional transition metal dichalcogenide micro-supercapacitors

1. A method of making a layered MoS 2 supercapacitor comprising the steps of:

forming into a supercapacitor by:

providing a substrate;

providing a Molybdenum source;

using a magnetron to induce a plasma to generate Molybdenum ions from the Molybdenum source;

sputtering the Molybdenum ions on the substrate to form a thin layer of Molybdenum, wherein the thin layer of Molybdenum is configured as a top layer to the substrate;

placing the substrate in a CVD chamber;

providing a sulphur source;

forming a sulphur vapor from the sulphur source, wherein the sulphur vapor is in communication with the CVD chamber; and

sulphurizing the top layer of Molybdenum to form a thin layer of Molybdenum disulfide (MoS 2 ).

2. A method of making a thin layer transition metal dichalcogenide (MX 2 ) supercapacitor comprising the steps of:

forming into a supercapacitor by:

providing a substrate;

providing a transition metal source;

using a magnetron to induce a plasma to generate transition metal ions;

sputtering the transition metal ions on the substrate to form a thin layer of transition metal, wherein the thin layer of transition metal is configured as a top layer to the substrate;

placing the substrate in a CVD chamber;

providing a chalcogen source;

forming a chalcogen vapor from the chalcogen source in communication with the CVD chamber; and

contacting the chalcogen vapor with the top layer of transition metal to form a thin layer transition metal dichalcogenide (MX 2 ).

3. The method of claim 2 , wherein the transition metal is Mo, W, or Nb.

4. The method of claim 2 , wherein the chalcogen is S, Se, or Te.

5. The method of claim 2 , wherein the transition metal dichalcogenide is MoS 2 , MoSe 2 , MoTe 2 , WS 2 , WSe 2 , WTe 2 , NbS 2 , NbSe 2 , or NbTe 2 .

6. The method of claim 2 , wherein the thin layer of transition metal is 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30 or more layers thick.

7. The method of claim 2 , wherein the transition metal dichalcogenide is 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30 or more layers thick.

8. The method of claim 2 , further comprising the step of controlling one or more parameters of the magnetron to apply 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30 or more layers of the transition metal.

9. The method of claim 2 , further comprising the step of adding a second transition metal to form a second thin layer on the thin layer.

10. The method of claim 9 , wherein the second transition metal is Mo, W, or Nb.

11. The method of claim 2 , wherein the substrate is a Si/SiO 2 substrate.

12. The method of claim 2 , wherein the magnetron uses a RF power source to creating a plasma.

13. The method of claim 2 , wherein the temperature of the substrate is at a temperature of between room temperature −800° C.

14. A method of making a MoS 2 supercapacitor, comprising:

providing a substrate;

forming an electrode film on the substrate by:

providing a Molybdenum source;

using a magnetron to induce a plasma to generate Molybdenum ions from the Molybdenum source;

sputtering the Molybdenum ions on the substrate to form a thin layer of Molybdenum, wherein the thin layer of Molybdenum is configured as a top layer to the substrate;

placing the substrate in a CVD chamber;

providing a sulphur source;

forming a sulphur vapor from the sulphur source, wherein the sulphur vapor is in communication with the CVD chamber; and

sulphurizing the top layer of Molybdenum to form a thin layer of Molybdenum disulfide MoS 2 on the substrate;

forming a current collector on both sides of the electrode film;

forming two separated electrodes by patterning the electrode film with an in-plane structure; and

reinforcing a bonding portion of the electrode film and the current collector through metal plating.

15. The method of claim 14 , further comprising supplying an electrolyte to the manufactured supercapacitor.

16. The method of claim 14 , wherein one of a water-soluble electrolyte, an organic electrolyte, an ionic liquid electrolyte, and a solid electrolyte is used for the electrolyte.

17. The MoS 2 supercapacitor made by the process of claim 14 .