MDO multilayer film
A multilayer film having Machine Direction Orientation (MDO) is prepared by first co-extruding a multilayer film, then stretching the multilayer film in the machine direction at a temperature lower than the melting point of the polyethylene resin that is used to prepare the film. At least one layer of the film is a first polyethylene composition having a density of from about 0.94 to about 0.97 g/cc and at least one second layer is prepared from a polyethylene composition having a lower density than the first polyethylene composition. This disclosure enables the manufacture of films having outstanding barrier properties (low Water Vapor Transmission Rate, WVTR, and low Oxygen Transmission Rate, OTR) and good physical properties.
1. A method for producing an oriented multi-layer film comprising:
A) co-extruding a multilayer film comprising:
1) a first layer prepared from a first high density polyethylene composition having a melt index, I 2 , of from about 0.2 to about 10 grams per 10 minutes, a density of from about 0.94 to about 0.97 g/cc and from about 100 to about 9000 parts per million of a nucleating agent, wherein the first layer is a core layer; and
2) a second layer prepared from a second polyethylene composition having a melt index, I 2 , of from about 0.2 to about 10 grams per 10 minutes and a density which is lower than the density of said first high density polyethylene composition by an amount of from about 0.010 to about 0.060 g/cc; and
B) stretching said multilayer film in the machine direction at a stretch ratio of from about 1:2 to about 1:12; wherein melt index is measured according to ASTM D1238 at 190° C. using a 2.16 kg weight and density is measured according to ASTM D792.
2. The method of claim 1 , wherein said stretching is done at a temperature below about 120° C.
3. The method of claim 1 , wherein said multilayer film is a three layer film having at least one skin layer prepared from said second polyethylene composition and a core layer prepared from said first high density polyethylene composition.
4. The method of claim 1 , wherein said multilayer film comprises at least five layers and wherein said multilayer film has two skin layers prepared from said second polyethylene composition and at least one core layer prepared from said first high density polyethylene composition.
5. The method of claim 1 , wherein said multilayer film has a thickness of from about 0.5 to about 3 mils after said stretching.
6. A film made by the method of claim 1 .
7. A package prepared from a film according to claim 6 .
8. A method for producing an oriented multilayer film comprising:
A) co-extruding a multilayer film comprising:
1) a first layer prepared from a first high density polyethylene composition having a melt index, I 2 , of from about 0.2 to about 10 grams per 10 minutes; a density of from about 0.95 to about 0.97 g/cc and a Mw/Mn of from about 5 to about 12, with the proviso that said first polyethylene composition is a blend of at least two blend components comprising a first blend component having a Mw/Mn of from about 2 to about 4 and a second blend component having a Mw/Mn of from about 2 to about 4, wherein the first layer is a core layer; and
2) a second layer prepared from a second polyethylene composition having a melt index, 12, of from about 0.2 to about 10 grams per 10 minutes and a densizy which is lower than the density of said first polyethylene composition by an amount of from about 0.010 to about 0.060 g/cc; and
B) stretching said multilayer film in the machine direction at a stretch ratio of from about 1:2 to about 1:12; wherein melt index is measured according to ASTM D1238 at 190° C. using a 2.16 kg weight and density is measured according to ASTM D792.
9. The method of claim 8 , wherein said first blend component has a melt index I2 and said second blend component has a melt index I 2 ′; wherein the ratio (I 2 /I 2 ′) is greater than about 10.
10. The method of claim 8 , wherein said stretching is done at a temperature below about 120° C.
11. The method of claim 8 , wherein said multilayer film is a three layer film having two skin layers prepared from said second polyethylene composition and a core layer prepared from said first high density polyethylene composition.
12. The method of claim 8 , wherein said multilayer film comprises at least five layers and wherein said multilayer film has two skin layers prepared from said second polyethylene composition and at least one core layer prepared from said first high density polyethylene composition.
13. The method of claim 8 , wherein said multilayer film has a thickness of from about 0.5 to about 3 mils after said stretching.
14. The method of claim 8 , wherein said first high density polyethylene composition further contains from about 100 to about 2000 parts per million of a nucleating agent.
15. A film made by the method of claim 8 .
16. A package prepared from a film according to claim 8 .
17. The method of claim 1 , wherein said nucleating agent comprises the calcium salt of hexahydrophthalic acid.