Slurry plasma spray of plasma resistant ceramic coating
Disclosed herein are methods for producing an ultra-dense and ultra-smooth ceramic coating. A method includes feeding a slurry of ceramic particles into a plasma sprayer. The plasma sprayer generates a stream of particles directed toward the substrate, forming a ceramic coating on the substrate upon contact.
1. A method of forming a plasma resistant ceramic coating on a component of a processing chamber, the method comprising:
feeding a slurry into a plasma sprayer at a flow rate of between about 5 mL/min and about 100 mL/min, wherein the slurry includes ceramic particles comprising at least one of Gd 3 Al 5 O 12 , La 2 O 3 , Er 4 Al 2 O 9 , Er 3 Al 5 O 12 , ErAlO 3 , Gd 4 Al 2 O 9 , GdAlO 3 , Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , or NdAlO 3 , and wherein the slurry further includes a polymer dispersant that is configured to facilitate uniform distribution of the ceramic particles; and
generating, with the plasma sprayer, a stream of the ceramic particles directed toward the component, wherein the stream of the ceramic particles forms the plasma resistant ceramic coating on the component upon contact with the component, wherein the plasma resistant ceramic coating comprises at least one of Gd 3 Al 5 O 12 , La 2 O 3 , Er 4 Al 2 O 9 , Er 3 Al 5 O 12 , ErAlO 3 , Gd 4 Al 2 O 9 , GdAlO 3 , Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , or NdAlO 3 .
2. The method of claim 1 , wherein the stream of the ceramic particles is generated by evaporating a solvent from the slurry upon passing the slurry through the plasma sprayer, and wherein the solvent comprises at least one of ethanol, methanol, de-ionized water, or acetonitrile.
3. The method of claim 1 , wherein the component comprises a ceramic, the method further comprising:
after forming the plasma resistant ceramic coating, heating the plasma resistant ceramic coating to a temperature up to about 2000° C.;
heat treating the component and the plasma resistant ceramic coating at the temperature of up to about 2000° C. for a time duration up to about 12 hours; and
forming a transition layer between the plasma resistant ceramic coating and the component via the heat treating.
4. The method of claim 1 , wherein a size of the ceramic particles is up to 15 micrometers.
5. The method of claim 1 , wherein a pH of the slurry is between 5 and 12.
6. The method of claim 1 , wherein a thickness of the plasma resistant ceramic coating is about 10-500 micrometers, a surface roughness of the plasma resistant ceramic coating is less than about 100 μin, and a porosity of the plasma resistant ceramic coating is less than about 0.8%.
7. The method of claim 1 , wherein the component is selected from a group comprising a lid, a nozzle, a chuck, a showerhead, a liner kit, or a ring.
8. The method of claim 1 , wherein the component comprises an additional ceramic coating disposed thereon, wherein the plasma resistant ceramic coating is formed over the additional ceramic coating, and wherein the additional ceramic coating is configured to minimize lattice mismatch with the plasma resistant ceramic coating.
9. The method of claim 8 , wherein:
a first porosity of the additional ceramic coating is greater than 0.8%, and a second porosity of the plasma resistant ceramic coating is less than or equal to 0.8%; and
a first surface roughness of the additional ceramic coating is greater than 100 μin, and a second surface roughness of the plasma resistant ceramic coating is less than or equal to 100 μin.
10. The method of claim 1 , further comprising:
generating, with the plasma sprayer, additional streams of ceramic particles to form a stack of ceramic layers on the component, the stack of ceramic layers comprising the plasma resistant ceramic coating.
11. The method of claim 10 , wherein the stack of ceramic layers comprises alternating layers of two different ceramic compounds selected from Gd 3 Al 5 O 12 , La 2 O 3 , Er 4 Al 2 O 9 , Er 3 Al 5 O 12 , ErAlO 3 , Gd 4 Al 2 O 9 , GdAlO 3 , Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , and NdAlO 3 .
12. The method of claim 1 , wherein the ceramic particles comprise at least one of Gd 3 Al 5 O 12 , GdAlO 3 or Gd 4 Al 2 O 9 .
13. The method of claim 1 , wherein the ceramic particles comprise La 2 O 3 .
14. The method of claim 1 , wherein the ceramic particles comprise at least one of Er 4 Al 2 O 9 or ErAlO 3 .
15. The method of claim 1 , wherein the ceramic particles comprise Er 3 Al 5 O 12 .
16. The method of claim 1 , wherein the ceramic particles comprise Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , or NdAlO 3 .
17. A method of forming a plasma resistant ceramic coating on a component of a processing chamber, the component having an amorphous ceramic coating formed thereon, the method comprising:
feeding a slurry into a plasma sprayer at a flow rate of about 5 mL/min to about 100 mL/min, wherein the slurry includes ceramic particles comprising at least one of Gd 2 O 3 , Gd 3 Al 5 O 12 , La 2 O 3 , Er 4 Al 2 O 9 , Er 3 Al 5 O 12 , ErAlO 3 , Gd 4 Al 2 O 9 , GdAlO 3 , Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , or NdAlO 3 ; and
generating, with the plasma sprayer, a stream of the ceramic particles directed toward the component and the amorphous ceramic coating, wherein the stream of the ceramic particles forms the plasma resistant ceramic coating on the component upon contact with the component, wherein a thickness of the plasma resistant ceramic coating is about 10 micrometers to about 500 micrometers, and wherein the plasma resistant ceramic coating comprises at least one of Gd 2 O 3 , Gd 3 Al 5 O 12 , La 2 O 3 , Er 4 Al 2 O 9 , Er 3 Al 5 O 12 , ErAlO 3 , Gd 4 Al 2 O 9 , GdAlO 3 , Nd 3 Al 5 O 12 , Nd 4 Al 2 O 9 , or NdAlO 3 ,
wherein the amorphous ceramic coating is configured to minimize lattice mismatch with the plasma resistant ceramic coating, and wherein the plasma resistant ceramic coating is a crystalline coating.
18. The method of claim 8 , further comprising:
performing plasma spraying using a dry powder feedstock to deposit the additional ceramic coating on the component prior to deposition of the plasma resistant ceramic coating.
19. The method of claim 8 , wherein the plasma resistant ceramic coating is a crystalline coating, and wherein the additional ceramic coating is an amorphous coating.
20. The method of claim 1 , wherein the polymer dispersant comprises at least one of polyacrylic acid, ammonium polymethacrylate, an omega-3 fatty acid, or polyethylene glycol.