Cast steel projection material
A cast steel shot media for performing a blasting treatment, including, at a weight ratio, 0.8% or more and 1.2% or less of C, 0.35% or more and 1.2% or less of Mn, and 0.4% or more and 1.5% or less of Si, in which a remainder has a hyper-eutectoid composition including Fe and inevitable impurities, and the cast steel shot media has a structure having a fine pearlite structure as a main constituent.
1. A cast steel shot media for performing a blasting treatment, comprising, at a weight ratio
0.8% or more and 1.2% or less of C,
0.35% or more and 1.2% or less of Mn, and
0.4% or more and 1.5% or less of Si,
wherein a remainder has a hyper-eutectoid composition including Fe and inevitable impurities, the cast steel shot media has a mixed structure with pro-eutectoid cementite having a fine pearlite structure as a main constituent, the cast steel shot media is formed in a substantially spherical shape having an average particle diameter of 1.0 mm or more and 2.5 mm of less, and an interlayer interval of the fine pearlite structure is 0.05 μm or more and 1.0 μm or less.
2. The cast steel shot media according to claim 1 , further comprising 0.05% or less of P and 0.05% or less of S at a weight ratio as the inevitable impurities.
3. The cast steel shot media according to claim 1 , wherein a Rockwell hardness of the cast steel shot media is HRC 35 or more and HRC 50 or less.
4. The cast steel shot media according to claim 1 , wherein the cast steel shot media is used for grinding of a casting.
5. The cast steel shot media according to claim 1 , wherein a passive film is formed on the surface.
6. The cast steel shot media according to claim 5 , wherein an average thickness of the passive film is 2 μm or more and 5 μm or less.
7. The cast steel shot media according to claim 1 , wherein the weight ratio of C is 0.8% or more and 1.1% or less.
8. The cast steel shot media according to claim 1 , wherein the weight ratio of Mn is 0.6% or more and 1.1% or less.
9. The cast steel shot media according to claim 1 , wherein the weight ratio of Si is 0.6% or more and 1.0% or less.
10. The cast steel shot media according to claim 1 , comprising at a weight ratio Cr of 0.05% or more and 0.8% or less.
11. The cast steel shot media according to claim 1 , further comprising 0.005% or more and 0.05% or less of P and 0.005% or more and 0.05% or less of S at a weight ratio as the inevitable impurities.