Rubber composition, method for producing same, and tire
Provided is a rubber composition that can improve fuel efficiency of a tire in low-temperature environments while ensuring adequate wet performance of the tire. The rubber composition contains: a rubber component (A) including at least 50 mass % of at least one isoprene-based rubber selected from the group consisting of natural rubber and synthetic isoprene rubber; a thermoplastic resin (B); and a filler (C) including at least 70 mass % of silica. The thermoplastic resin (B) is contained in an amount of from 5 parts by mass to 40 parts by mass relative to 100 parts by mass of the rubber component (A). The rubber composition has a tan δ at 0° C. of no greater than 0.5, a difference between tan δ at 30° C. and tan δ at 60° C. of no greater than 0.070, and a storage modulus at 1% dynamic strain and 0° C. of no greater than 20 MPa.
1. A rubber composition comprising:
a rubber component (A) including at least 50 mass % of at least one isoprene-based rubber selected from the group consisting of natural rubber and synthetic isoprene rubber;
a thermoplastic resin (B); and
a filler (C) including at least 70 mass % of silica, wherein
the thermoplastic resin (B) is contained in an amount of from 5 parts by mass to 40 parts by mass relative to 100 parts by mass of the rubber component (A),
tan δ of the rubber composition at 0° C. is no greater than 0.5,
a difference between tan δ of the rubber composition at 30° C. and tan δ of the rubber composition at 60° C. is no greater than 0.070, and
a storage modulus of the rubber composition at 1% dynamic strain and 0° C. is no greater than 20 MPa.
2. The rubber composition of claim 1 , wherein
a difference between tan δ of the rubber composition at 0° C. and tan δ of the rubber composition at 30° C. is no greater than 0.30.
3. The rubber composition of claim 1 , wherein
a difference between tan δ of the rubber composition at 0° C. and tan δ of the rubber composition at 60° C. is no greater than 0.35.
4. The rubber composition of claim 1 , further comprising
from 1 part by mass to 5 parts by mass of a softener (D) relative to 100 parts by mass of the rubber component.
5. The rubber composition of claim 4 , wherein
the softener (D) is a mineral-derived or petroleum-derived softener.
6. The rubber composition of claim 1 , wherein
the filler (C) further includes carbon black, and the carbon black is contained in an amount of from 1 part by mass to 10 parts by mass relative to 100 parts by mass of the rubber component.
7. The rubber composition of claim 1 , wherein
the thermoplastic resin (B) is at least one resin selected from the group consisting of a C 5 resin, a C 9 resin, a C 5 -C 9 resin, a dicyclopentadiene resin, a rosin resin, an alkyl phenolic resin, and a terpene phenolic resin.
8. A method for producing the rubber composition of claim 1 , comprising
kneading the rubber component (A) including at least 50 mass % of at least one isoprene-based rubber selected from the group consisting of natural rubber and synthetic isoprene rubber, the thermoplastic resin (B), and the filler (C) including at least 70 mass % of silica at from 150° C. to 165° C., without a vulcanization compounding agent including a vulcanizing agent and a vulcanization accelerator.
9. A tire comprising tread rubber in which the rubber composition of claim 1 is used.
10. The rubber composition of claim 1 , wherein the silica is contained in an amount of from 40 parts by mass to 70 parts by mass relative to 100 parts by mass of the rubber component.
11. The rubber composition of claim 1 , wherein the silica is contained in an amount of from 45 parts by mass to 60 parts by mass relative to 100 parts by mass of the rubber component.