Electrically heated catalytic converter and method of manufacturing the same
Provided is an electrically heated catalytic converter including at least a conductive substrate and an electrode member that is fixed to the substrate, in which a protective film is formed on a surface of at least a portion of the electrode member. In the electrically heated catalytic converter, at least a portion of the protective film is formed of Al 2 O 3 , SiO 2 , a composite material of Al 2 O 3 and SiO 2 , or a composite oxide including Al 2 O 3 , SiO 2 , or a composite material of Al 2 O 3 and SiO 2 as a major component, the protective film has an amorphous structure or a partially crystalline glass structure having a crystallization rate of 30 vol % or lower with respect to the entire portion of the protective film, and a thickness of the protective film is in a range of 100 nm to 2 μm.
1. An electrically heated catalytic converter comprising:
a conductive substrate that includes a catalyst coating layer;
an electrode member that is fixed to the substrate; and
a protective film that is provided on a surface of at least a portion of the electrode member, wherein
the protective film is formed of i) Al 2 O 3 , ii) SiO 2 , iii) a composite material of Al 2 O 3 and SiO 2 , or iv) a composite oxide including Al 2 O 3 , SiO 2 , or a composite material of Al 2 O 3 and SiO 2 as a major component,
the protective film has a configuration in which an entire portion is formed of an amorphous structure or in which a partially crystalline glass structure having a crystallization rate of 30 vol % or lower with respect to the entire portion of the protective film is provided, and
a thickness of the protective film is in a range of 100 nm to 2 μm.
2. The electrically heated catalytic converter according to claim 1 , wherein
the conductive substrate is a conductive ceramic including SiC as a major component.
3. The electrically heated catalytic converter according to claim 1 , wherein
the electrode member is a single member made of a metal or a ceramic or a composite member made of a metal and a ceramic,
the electrode member is constituted with a surface electrode and a wiring fixing layer, and
a porosity of the surface electrode and the wiring fixing layer is 5% or higher.
4. A method of manufacturing an electrically heated catalytic converter,
the electrically heated catalytic converter including at least a conductive substrate that includes a catalyst coating layer and an electrode member that is fixed to the substrate, in which a protective film is formed on a surface of at least a portion of the electrode member, and
the method comprising:
preparing a sol-gel solution by adding any one of i) Al 2 O 3 , ii) SiO 2 , iii) a composite material of Al 2 O 3 and SiO 2 , and iv) a composite oxide including Al 2 O 3 , SiO 2 , or a composite material of Al 2 O 3 and SiO 2 as a major component to a solvent; and
manufacturing the electrically heated catalytic converter by applying the sol-gel solution to the surface of at least the portion of the electrode member, drying the sol-gel solution to form a coating film, and firing the coating film at a temperature of 500° C. or lower to form the protective film.
5. The method according to claim 4 , wherein
the conductive substrate is a conductive ceramic including SiC as a major component.
6. The method according to claim 4 , wherein
the electrode member is a single member made of a metal or a ceramic or a composite member made of a metal and a ceramic, and
the electrode member is constituted with a surface electrode and a wiring fixing layer
the electrode member is a porous member in which a porosity of the surface electrode and the wiring fixing layer is 5% or higher.
7. The method according to claim 4 , wherein
the sol-gel solution is applied to the surface of at least the portion of the electrode member and is dried to form the coating film, and the coating film is fired at a temperature of 100° C. to 200° C. to form the protective film.
8. The method according to claim 4 , wherein
a thickness of the protective film is in a range of 100 nm to 2 μm.
9. The method according to claim 4 , wherein
the protective film has a configuration in which an entire portion is formed of an amorphous structure or in which a partially crystalline glass structure having a crystallization rate of 30 vol % or lower with respect to the entire portion of the protective film is provided.