Preparation method and application of light-responsive LED based on GaN/CsPbBr

1. A preparation method for a light-responsive LED based on a GaN/CsPbBr x I 3-x heterojunction, comprising steps of:

(1) selecting a GaN base layer and washing, particularly comprising steps of:

selecting a GaN base layer on a sapphire substrate, and ultrasonically cleaning; then processing with ultraviolet and ozone, and obtaining a preprocessed GaN base layer;

(2) preparing an indium bottom electrode, particularly comprising steps of:

coating molten indium uniformly on one side of the preprocessed GaN base layer obtained through the step (1); cooling to a room temperature, and obtaining the indium bottom electrode;

(3) generating an all-inorganic perovskite CsPbBr x I 3-x polycrystalline film with an anti-solvent, particularly comprising steps of:

according to a proportion, successively dissolving all-inorganic perovskite CsPbBr 3 powders and CsPbI 3 powders in DMSO (dimethylsulfoxide); after standing for 1-3 hours, filtering by a filter, and obtaining a colorless transparent solution; thereafter, dropping a small amount of the colorless transparent solution uniformly on the other side of the GaN base layer; placing the GaN base layer on a spin coater, and running for 40-80 seconds with a rotation speed of 3000-5000 rpm, wherein the anti-solvent is dropped on the GaN base layer after running for 15-30 seconds; placing an obtained sample in an inert atmosphere, and annealing at 80-120° C. for 5-15 minutes; and obtaining the all-inorganic perovskite CsPbBr x I 3-x polycrystalline film;

(4) preparing a carbon top electrode, particularly comprising steps of:

with using a mask, blade-coating carbon paste on the CsPbBr x I 3-x polycrystalline film obtained through the step (3); placing the sample in an argon atmosphere, and annealing, so as to remove solvent in the carbon paste; and

(5) testing, particularly comprising steps of:

after finishing testing, obtaining a complete LED device;

wherein: the obtained LED consists of the GaN base layer on the sapphire substrate, the all-inorganic perovskite CsPbBr x I 3-x polycrystalline film, the indium bottom electrode and the carbon top electrode, forming an In/GaN/CsPbBr x I 3-x /C structure; in the CsPbBr x I 3-x polycrystalline film, 0<x<3; the all-inorganic perovskite CsPbBr x I 3-x polycrystalline film and the indium bottom electrode are arranged on the GaN base layer in parallel; and the carbon top electrode is arranged on the all-inorganic perovskite CsPbBr x I 3-x polycrystalline film.

2. The preparation method, as recited in claim 1 , wherein: in the step (3), a weight ratio of the CsPbBr 3 powders to the CsPbI 3 powders is 1:0, 1:1, 1:3, or 0:1.

3. The preparation method, as recited in claim 1 , wherein: in the step (3), the anti-solvent is ethyl ether, ethyl acetate, or methylbenzene.

4. The preparation method, as recited in claim 1 , wherein: in the step (3), the all-inorganic perovskite CsPbBr 3 powders are prepared through steps of:

dissolving PbBr 2 in an appropriate amount of HBr, heating and stirring until fully dissolved, and obtaining a solution A; dissolving CsBr in an appropriate amount of deionized water, heating and stirring until fully dissolved, and obtaining a solution B; rapidly adding the solution B into the solution A, stirring until completely reacted, and obtaining yellow powdery precipitates; washing the precipitates with methyl alcohol or ethyl alcohol; after suction filtration, annealing obtained powders in an inert atmosphere at 60-80° C. for 20-40 minutes, so as to remove the residual methyl alcohol or ethyl alcohol, and obtaining the all-inorganic perovskite CsPbBr 3 powders.

5. The preparation method, as recited in claim 4 , wherein: a molar ratio of PbBr 2 to CsBr is 1:2.