Humins-containing foam
A foam includes a cellular structure and having a density of at most 0.50 g/cm 3 , where the cellular structure is provided by a solid material that includes humins. Such a foam is prepared in a process, which includes: providing a starting material containing humins; and heating the starting material to a temperature in the range of 150 to 450° C. The foam can be used in articles for a variety of applications such as substrate for plant growth, as adsorbent for treating waste water or waste gases, as support for solid catalysts, as insulation material, or packaging material.
1. A foam comprising a cellular structure and having a density of at most 0.50 g/cm 3 , wherein the cellular structure is provided by a solid material that comprises humins and a fibrous material.
2. The foam according to claim 1 , which has a density in the range of 0.025 to 0.50 g/cm 3 .
3. The foam according to claim 1 , wherein the cellular structure comprises cells with an average cell diameter in the range of 1 to 5,000 μm.
4. The foam according to claim 1 , wherein the foam has a specific surface area, as determined according to the BET method, of 1 to 50 m 2 /g.
5. The foam according to claim 1 , wherein the fibrous material has been selected from the group consisting of glass fibers, graphite fibers, aluminum fibers, organic fibers and combinations thereof.
6. The foam according to claim 5 , wherein the organic fibers are selected from the group consisting of polyamide fibers, polyolefin fibers, polyvinyl chloride fibers, polyester fibers and combinations thereof.
7. The foam according to claim 6 , wherein the weight ratio between humins and fibrous material is in the range of 0.1:1 to 10:1.
8. The foam according to claim 1 , wherein the solid material that provides the cellular structure comprises spent mushroom substrate, starch, hemp, nettles, hay, straw, manure, chicken feathers, chitinous materials and combinations thereof.
9. A process for the preparation of a foam comprising a cellular structure and having a density of at most 0.50 g/cm 3 , wherein the cellular structure is provided by a solid material that comprises humins and a fibrous material, which process comprises:
providing a starting material containing humins and a fibrous material; and
heating the starting material to a temperature in the range of 150 to 450° C.
10. The process according to claim 9 , wherein the starting material is heated to a temperature in the range of from 180 to 350° C.
11. The process according to claim 9 , wherein the starting material is heated at a pressure of at most 1.5 bar.
12. The process according to claim 9 , wherein the starting material is heated for a period ranging from 0.01 to 5 hrs.
13. The process according to claim 9 , wherein the starting material comprises humins that have been obtained in the dehydration of carbohydrates, in particular in the dehydration of carbohydrates in the manufacture of levulinic acid, 5-hydroxymethylfurfural (HMF) and ethers or esters of HMF.
14. The process according to claim 9 , wherein the starting material containing humins is mixed with a blowing agent before being heated.
15. The process according to claim 14 , wherein the blowing agent is selected from the group consisting of water, 5-hydroxymethyl furfural (HMF), C 1 -C 4 alkyl ethers of HMF, C 1 -C 4 -alkyl esters of HMF, C 1 -C 4 -alkyl esters of levulinic acid, levulinic acid and combinations thereof.
16. The process according to claim 14 , wherein the starting material is mixed with the blowing agent in an amount of 0.1 to 10 parts by weight of blowing agent per part by weight of starting material.
17. The process according to claim 9 , wherein the starting material is mixed with a monomer containing at least one reactive group towards a hydroxyl, carbonyl or carboxyl group.
18. The process according to claim 17 , wherein the reactive group is an epoxy group, an isocyanate group, an amine group, a hydroxyl group or a combination of one or more of such groups.
19. The process according to claim 17 , wherein the monomer containing at least one reactive group is mixed with the starting material in an amount of 0.1 to 5% wt, based on the starting material.
20. An article comprising a foam according to claim 1 for use as substrate for plant growth, as adsorbent for treating waste water or waste gases, as support for solid catalysts, as insulation material, or as packaging material.
21. An article comprising a foam obtained in a process according to claim 9 for use as substrate for plant growth, as adsorbent for treating waste water or waste gases, as support for solid catalysts, as insulation material, or as packaging material.