Texturing method for diamond wire cut polycrystalline silicon slice
It discloses a texturing method for a diamond wire cut polycrystalline silicon slice, including the following steps: firstly, immersing the diamond wire cut polycrystalline silicon slice into a mixed aqueous solution of an alkali solution and an alkali reaction control agent, removing a damaged layer on a surface of the silicon slice, and then immersing the silicon slice into a hydrofluoric acid solution containing inorganic ions and organic molecules for reaction; secondly, pretreating the polycrystalline silicon surface by a mixed solution of hydrofluoric acid and hydrogen peroxide, adding a pore-forming regulator at the same time, and finally texturing the surface of the silicon slice by a mixed acid solution of hydrofluoric acid and nitric acid.
1. A texturing method for a diamond wire cut polycrystalline silicon slice, characterized by comprising the following steps:
(1) a first procedure: immersing the diamond wire cut polycrystalline silicon slice into a mixed aqueous solution of an alkali solution and an alkali reaction control agent, and removing a damaged layer on a surface of polycrystalline silicon to form a silicon slice convex microstructure; the alkali reaction control agent comprises a mixture of polycarboxylic acid, isooctyl polyoxyethylene ether phosphate, and -allyl alcohol polyoxyalkyl ether; or a mixture of polycarboxylic acid and polyethylene glycol;
(2) a second procedure: immersing the polycrystalline silicon slice with the convex microstructure into a hydrofluoric acid solution containing inorganic ions and organic molecules to deposit metal particles on the surface of the silicon slice;
(3) a third procedure: forming pores in the prepared silicon slice in a mixed solution containing a pore-forming regulator, hydrofluoric acid and hydrogen peroxide; the pore-forming regulator comprises one or more of glucuronic acid, galacturonic acid, fatty acid amide, fatty alcohol polyoxyethylene ether, sodium alginate, sodium cellulose, glucosamine, sodium carboxylate, octadecatrienoic acid or oleic acid; and
(4) a fourth procedure: after cleaning the silicon slice, texturing the surface of the silicon slice by a mixed acid solution of hydrofluoric acid and nitric acid.
2. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (1), the concentration of the alkali reaction control agent is 0.1-1.0%.
3. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (2), the inorganic ions include inorganic cations and inorganic anions, wherein the inorganic cations are one or more of copper ions, silver ions and silver ammonium ions, and the inorganic anions are chloroauric acid ions and/or nitrate ions.
4. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (2), the concentration of the inorganic ions is 1×10 6 −5×10 −2 mol/L.
5. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (2), the organic molecules are one or more of methanol, ethanol, polyethylene glycol, formic acid, acetaldehyde, vitamin C, citric acid, glucose, methylamine or ethylenediamine.
6. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (2), the concentration of the organic molecules is 1×10 4 −5×10 −2 mol/L.
7. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (3), the concentration of the pore-forming regulator is 0.1-1.0%.
8. The texturing method for the diamond wire cut polycrystalline silicon slice according to claim 1 , characterized in that in step (4), the concentration of the hydrofluoric acid is 1.5-5 mol/L, and the concentration of the nitric acid is 4-7 mol/L.