Surface-modified nanodiamond, organic solvent dispersion thereof, and method for producing surface-modified nanodiamond
There are provided a surface-modified nanodiamond exhibiting easy dispersibility in an organic solvent, an organic solvent dispersion thereof, and a method for producing the surface-modified nanodiamond. The surface-modified nanodiamond according to the present invention includes a nanodiamond, and a group bound to a particulate surface of the nanodiamond and represented by formula ( 1 ): —NHCOR ( 1 ) R is an organic group having a carbon atom at a binding site with a neighboring carbonyl carbon atom indicated in the formula; and the left end, in the formula, of the group serves to form bonding to the nanodiamond. The nanodiamond is preferably a detonation nanodiamond or a high-temperature high-pressure nanodiamond.
1. A surface-modified nanodiamond comprising:
a nanodiamond; and
a group being bound to a particulate surface of the nanodiamond and represented by formula (1):
—NHCOR (1)
wherein R is an organic group having a carbon atom at a binding site with a neighboring carbonyl carbon atom indicated in the formula; and the left end, in the formula, of the group serves to form bonding to the nanodiamond.
2. The surface-modified nanodiamond according to claim 1 , wherein the nanodiamond is a detonation nanodiamond or a high-temperature high-pressure nanodiamond.
3. The surface-modified nanodiamond according to claim 1 or 2 , wherein R in the formula (1) represents a straight-chain or branched-chain alkyl group having 1 to 22 carbon atoms or a 3- to 22-membered cycloalkyl group.
4. An organic solvent dispersion of nanodiamonds, being made by dispersing the surface-modified nanodiamond according to claim 1 in an organic solvent.
5. The organic solvent dispersion of nanodiamonds according to claim 4 , wherein the organic solvent has an SP value [(cal/cm 3 ) 0.5 : Fedors calculation value] at 25° C. of 7 to 23.
6. The organic solvent dispersion of nanodiamonds according to claim 4 or 5 , wherein the organic solvent has a relative permittivity at 25° C. of 1 to 40.
7. A method for producing a surface-modified nanodiamond, the method comprising:
reacting a nanodiamond with a nitrile compound in the presence of an acid catalyst to obtain the surface-modified nanodiamond according to claim 1 , the nitrile compound being represented by formula (2):
R—CN (2)
wherein R is an organic group having a carbon atom at a binding site with a cyano group indicated in the formula.
8. The method for producing a surface-modified nanodiamond according to claim 7 , wherein the reaction of the nanodiamond with the nitrile compound represented by the formula (2) is carried out after a deagglutinating and/or crushing treatment for the nanodiamond or during a deagglutinating and/or crushing treatment for the nanodiamond.