Mineral coated scaffolds
Provided is a composition for a scaffold having a mineral coating similar to bone. Also provided is a method for mineral coating a scaffold so as to promote mineral coating of the scaffold with a plate-like nanostructure and a carbonate-substituted, calcium-deficient hydroxyapatite phase.
1. A method for producing a mineral coated scaffold comprising:
contacting a scaffold comprising a matrix material and a modified simulated body fluid, wherein the modified simulated body fluid comprises 20 mM Tris, at least 5 mM CaCl 2 and at least 2 mM KH 2 PO 4 ; and
incubating the scaffold and the modified simulated body fluid for a period of time under conditions sufficient to form a mineral coated scaffold,
wherein the modified simulated body fluid is adjusted to a pH of about 6.5 to about 7.2,
wherein the mineral coating comprises a carbonate-substituted, calcium-deficient hydroxyapatite component, and the mineral coating has a plate-like nanostructure and a porosity between about 20% and about 28%.
2. The method of claim 1 , wherein the matrix material is a biodegradable matrix material.
3. The method of claim 1 , wherein the matrix material comprises polycaprolactone (PCL), polyetheretherketone (PEEK), or titanium (Ti).
4. The method of claim 1 , further comprising combining NaCl, KCl, MgCl 2 , MgSO 4 , NaHCO 3 , Tris, CaCl 2 , and KH 2 PO 4 to form the modified simulated body fluid.
5. The method of claim 4 , wherein:
(i) NaCl has a concentration of about 100 mM to about 200 mM;
(ii) KCl has a concentration of about 1 mM to about 8 mM;
(iii) MgCl 2 has a concentration of about 0.2 mM to about 5 mM;
(iv) MgSO 4 has a concentration of about 0.2 mM to about 5 mM;
(v) NaHCO 3 has a concentration of about 1 mM to about 100 mM;
(vi) CaCl 2 has a concentration of about 5 mM to about 20 mM;
(vii) KH 2 PO 4 has a concentration of about 2 mM to about 10 mM; and
(viii) Tris has a concentration of 20 mM.
6. The method of claim 4 , wherein:
(i) NaCl has a concentration of about 141 mM;
(ii) KCl has a concentration of about 4.0 mM;
(iii) MgCl 2 has a concentration of about 1.0 mM;
(iv) MgSO 4 has a concentration of about 0.5 mM;
(v) NaHCO 3 has a concentration of about 4.2 mM;
(vi) CaCl 2 has a concentration of about 5 mM;
(vii) KH 2 PO 4 has a concentration of about 2.0 mM; and
(viii) Tris has a concentration of 20 mM.
7. The method of claim 1 , wherein the period of time is from about 5 days to about 28 days.
8. The method of claim 1 , wherein the period of time is selected from the group consisting of about 1 day; about 2 days; about 3 days; about 4 days; about 5 days; about 6 days; about 7 days; about 8 days; about 9 days; about 10 days; about 11 days; about 12 days; about 13 days; about 14 days; about 15 days; about 16 days; about 17 days; about 18 days; about 19 days; about 20 days; about 21 days; about 22 days; about 23 days; about 24 days; about 25 days; about 26 days; about 27 days; and about 28 days.
9. The method of claim 1 , wherein the period of time is about 5 days to about 14 days.
10. The method of claim 1 , further comprising hydrolyzing the scaffold.
11. The method of claim 1 , wherein the incubation comprises heating the modified simulated body fluid to a physiologic temperature.
12. The method of claim 11 , wherein the physiologic temperature is about 37° C. or the pH is about 6.8.
13. The method of claim 1 , wherein incubating comprises replacing the modified simulated body fluid, replenishing the modified simulated body fluid, removing the modified simulated body fluid, or adding the modified simulated body fluid, wherein incubating comprises maintaining a concentration of modified simulated body fluid.
14. The method of claim 1 , wherein the coating comprises about 97% hydroxyapatite.
15. The method of claim 1 , wherein the coating comprises about 3% octacalcium phosphate.
16. The method of claim 1 , wherein the coating comprises between about 100 nm and about 350 nm pore diameter.
17. The method of claim 1 , wherein the coating comprises (i) about 1.37 to about 1.61 Ca/P; or (ii) about 1.1 to about 1.3 Ca/P (calcium to phosphate ratio).
18. A mineral coated scaffold produced according to claim 1 , comprising a scaffold comprising a matrix material, wherein the mineral coating of the scaffold comprises a carbonate-substituted, calcium-deficient hydroxyapatite component.
19. A mineral coated scaffold comprising a matrix material, wherein the mineral coating comprises a carbonate-substituted, calcium-deficient hydroxyapatite component; and wherein the mineral coating formed from an incubated simulated body fluid comprising 5 mM CaCl 2 and about 2 mM KH 2 PO 4 and the mineral coating comprises a porosity between about 20% and about 28% and a plate-like nanostructure.
20. The mineral coated scaffold of claim 19 , wherein the coating comprises:
(i) about 97% hydroxyapatite;
(ii) about 3% octacalcium phosphate;
(iii) between about 100 nm and about 350 nm pore diameter; or
(iv) about 1.1 to about 1.3 Ca/P; or about 1.37 to about 1.61 Ca/P.
21. The method of claim 1 , wherein the modified simulated body fluid further comprises one or more constituents of blood plasma.
22. The method of claim 21 , wherein the one or more constituents of blood plasma are ionic.
23. The method of claim 1 , wherein the modified simulated body fluid comprises 20 mM Tris, at least 7.5 mM CaCl 2 and at least 3 mM KH 2 PO 4 .
24. The method of claim 1 , wherein the scaffold is hydrolyzed in a 1.0 M NaOH solution for 60 minutes prior to contacting with the modified simulated body fluid.
25. The mineral coated scaffold of claim 19 , wherein the coating comprises at least one of silver particles or demineralized bone matrix.
26. The mineral coated scaffold of claim 25 , wherein the silver particles are provided in an amount effective to provide at least one of antimicrobial, antibacterial, biostatic, or anti-infection properties.
27. The mineral coated scaffold of claim 25 , wherein the silver particles are provided as silver microparticles or silver nanoparticles.
28. A method, comprising:
functionalizing a surface of a scaffold, wherein the scaffold comprises a matrix material;
contacting the scaffold with a modified simulated body fluid, wherein the modified simulated body fluid comprises 20 mM Tris, at least 5 mM CaCl 2 and at least 2 mM KH 2 PO 4 ; and
incubating the scaffold and the modified simulated body fluid for a period of time under conditions sufficient to form a mineral coated scaffold, wherein the mineral coating comprises a carbonate-substituted, calcium-deficient hydroxyapatite component, and the mineral coating has a plate-like nanostructure and a porosity between about 20% and about 28% and the modified simulated body fluid is at a pH of 6.5 to 7.2.
29. A method, comprising: hydrolyzing a scaffold;
contacting the scaffold comprising a matrix material and a modified simulated body fluid,
wherein the modified simulated body fluid comprises 20 mM Tris, at least 5 mM CaCl 2 and at least 2 mM KH 2 PO 4 ; and
incubating the scaffold and the modified simulated body fluid for a period of time under conditions sufficient to form a mineral coated scaffold, the modified simulated body fluid being at a pH of 6.5 to 7.2,
wherein the mineral coating comprises a carbonate-substituted, calcium-deficient hydroxyapatite component, and the mineral coating has a plate-like nanostructure and a porosity between about 20% and about 28%.