Resin composition and membrane structure comprising the same
Provided is an ECTFE resin composition that is superior in transparency and resistant to yellowing for an extended period of time. The ECTFE resin composition generates a smaller amount of acidic gases, for example, when it is extrusion molded at high temperature. It is an ethylene-chlorotrifluoroethylene copolymer resin composition including a bisphenol-based antioxidant. It is preferably an ethylene-chlorotrifluoroethylene copolymer resin composition additionally including a phosphorus-based antioxidant.
1. An ethylene-chlorotrifluoroethylene copolymer resin composition having a sheet shape and comprising a bisphenol-based antioxidant, and a phosphorus-based antioxidant,
wherein the bisphenol-based antioxidant is at least one compound selected from 3,9-bis[2-[3-(tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy)]-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5,5]undecane, 4,4′-butylidene bis(3-methyl-6-tert-butylphenol) and 2,2′-bis(4-hydroxyphenyl)propane, and
wherein the phosphorus-based antioxidant is contained in an amount in the range of 0.01 to 1.0 mass %.
2. The resin composition according to claim 1 , wherein the bisphenol-based antioxidant is contained in an amount in the range of 0.01 to 1.0 mass %.
3. The resin composition according to claim 1 , wherein the phosphorus-based antioxidant is a phosphorous ester-based antioxidant.
4. The resin composition according to claim 1 , wherein the phosphorus-based antioxidant is at least one compound selected from 6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenzo[d,f][1,3,2]dioxaphosphepin, 3,9-bis(2,6-di-tert-butyl-4-methylphenoxy)-2,4,8,10-tetraoxa-3,9-diphosphaspiro[5,5]undecane, and tris(2,4-di-tert-butylphenyl) phosphite.
5. The resin composition according to claim 1 , comprising no acid acceptor.
6. A membrane structure, comprising the resin composition according to claim 1 .
7. A building comprising the resin composition according to claim 1 as a roofing material, an outer wall material, or a coating material.
8. A front sheet or a back sheet for solar cells, comprising the resin composition according to claim 1 .
9. An agricultural film, comprising the resin composition according to claim 1 .
10. The resin composition according to claim 1 , wherein the ethylene-chlorotrifluoroethylene copolymer has a molar ratio of ethylene and chlorotrifluoroethylene, in copolymerization, of 30/70 to 70/30.
11. The resin composition according to claim 1 , wherein the phosphorus-based antioxidant is 6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenzo[d,f][1,3,2]dioxaphosphepin to provide yellowing resistance and transparency and to reduce an amount of acidic gasses generated.
12. An ethylene-chlorotrifluoroethylene copolymer resin composition having a sheet shape and comprising a bisphenol-based antioxidant, and a phosphorus-based antioxidant,
wherein the bisphenol-based antioxidant is at least one compound selected from 3,9-bis[2-[3-(tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy)]-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5,5]undecane, 4,4′-butylidene bis(3-methyl-6-tert-butylphenol) and 2,2′-bis(4-hydroxyphenyl)propane, and
wherein the phosphorus-based antioxidant is at least one compound selected from 6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenzo[d,f][1,3,2]-dioxaphosphepin and 3,9-bis(2,6-di-tert-butyl-4-methylphenoxy)-2,4,8,10-tetraoxa-3,9-diphosphaspiro[5,5]undecane.
13. The resin composition according to claim 12 , wherein the bisphenol-based antioxidant is contained in an amount in the range of 0.01 to 1.0 mass %.
14. The resin composition according to claim 12 , comprising no acid acceptor.
15. A membrane structure, comprising the resin composition according to claim 12 .
16. A building comprising the resin composition according to claim 12 as a roofing material, an outer wall material, or a coating material.
17. A front sheet or a back sheet for solar cells, comprising the resin composition according to claim 12 .
18. An agricultural film, comprising the resin composition according to claim 12 .
19. The resin composition according to claim 12 , wherein the ethylene-chlorotrifluoroethylene copolymer has a molar ratio of ethylene and chlorotrifluoroethylene, in copolymerization, of 30/70 to 70/30.
20. The resin composition according to claim 12 , wherein the phosphorus-based antioxidant is 6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenzo[d,f][1,3,2]dioxaphosphepin to provide yellowing resistance and transparency and to reduce an amount of acidic gasses generated.