Anti-fatigue in-situ aluminum-based composite material for heavy-load hubs and preparation method therefor
Provided are an anti-fatigue in-situ aluminum-based nanocomposite material for heavy-load automobile hubs and a preparation method therefor. By means of the fine adjustment of components and a forming process, in situ nano-compositing, micro-alloying and rapid compression moulding techniques are combined. That is, after the addition of Zr and B, an in-situ reaction occurs to form a nano ZrB 2 ceramic reinforcement, which is distributed in aluminum crystals and crystal boundaries and bonded to a metallurgical interface kept firm with the matrix.
1. An anti-fatigue in-situ aluminum based composite material for automobile hubs, comprising, by mass percent, the following chemical components: 6.8-7.5 of Si, 3.0-5.0 of Zr, 0.5-1.0 of B, 0.3-0.45 of Mg, 0.18-0.25 of Er, 0.18-0.25 of Y, 0.15-0.22 of Cr, 0.1-0.12 of Mn, 0.1-0.15 of Ti, 0.08-0.12 of Fe, 0.05-0.1 of Cu, and the balance of Al,
wherein said composite material is prepared according to the following steps:
microalloying A356.2 aluminum alloy melt;
carrying out in-situ nano compounding for the microalloyed A356.2 aluminum alloy melt;
carrying out pressurized gravity casting rapid sequential solidification molding for the A356.2 aluminum alloy melt that has been subjected to in-situ nano compounding; and
carrying out thermal treatment for the hub formed with a casting, combining microalloying, in-situ nano compounding and pressurized gravity casting rapid sequential solidification molding,
wherein, for the step of pressurized gravity casting rapid sequential solidification molding, a feed port cooling system and a pressurization mechanism are arranged additionally on the basis of the original gravity casting equipment and are transformed to achieve a sectional cooling of a mold, and
wherein an inlet portion of the alloy melt or composite material injected into a cavity is first solidified to seal the cavity, the pressurization mechanism is then started, so that the closed melt regulates the feed port cooling system of the mold under a pressure of 50-250 MPa to achieve sequential solidification of the casting.
2. The anti-fatigue in-situ aluminum based composite material according to claim 1 , wherein the step of microalloying the A356.2 aluminum alloy melt comprises the following steps:
refining molten and heat-preserved A356.2 aluminum alloy melt for degassing;
uniformly scattering a layer of covering agent on a surface of the A356.2 aluminum alloy melt;
pressing an intermediate alloy of microalloying elements into the refined and degassed A356.2 aluminum alloy melt via an immersion bell; and
stirring uniformly with a graphite rotor and allowing to stand for later use.
3. The anti-fatigue in-situ aluminum based composite material according to claim 2 , wherein a melting and heat-preservation temperature of the A356.2 aluminum alloy is 750-760 degrees C., and wherein the intermediate alloy of the microalloying element comprises Al—Zr, Al—Er, Al—Y, Al—Cr, and Al—Mn.
4. The anti-fatigue in-situ aluminum based composite material according to claim 2 , wherein the intermediate alloy of the microalloying element comprises Al-15Zr, Al-20Er, Al-20Y, Al-20Cr, and Al-10Mn.
5. The anti-fatigue in-situ aluminum based composite material according to claim 2 , wherein the step of microalloying the A356.2 aluminum alloy melt adjusts ingredients of the A356.2 aluminum alloy melt by introducing Er, Y, and Zr as additive ingredients, and increasing the content of Cr and Mn in the A356.2 aluminum alloy melt, after which the mass percent of elements in the A356.2 aluminum alloy melt is as follows: 3.0-5.0 of Zr, 0.18-0.25 of Er, 0.18-0.25 of Y, 0.15-0.22 of Cr, and 0.1-0.12 of Mn.
6. The anti-fatigue in-situ aluminum based composite material according to claim 1 , wherein the step of carrying out in-situ nano compounding for the microalloyed A356.2 aluminum alloy melt comprises the following steps:
pressing a boron containing alloy or boron salt via a graphite immersion bell into the microalloyed A356.2 aluminum alloy melt;
starting a graphite stirring rotor to promote melting of the boron containing alloy or to promote the boron salt to fully contact with the A356.2 aluminum alloy melt and effectively absorb boron;
making the boron from the boron containing alloy or boron salt react in-situ with Zr introduced during the microalloying of the A356.2 aluminum alloy melt to synthesize a ZrB 3 nano-ceramic reinforcement; and
acquiring the resulting composite melt and allowing it to stand for later use.
7. The anti-fatigue in-situ aluminum based composite material according to claim 1 , wherein the step of in-situ nano compounding comprises introducing boron into the microalloyed A356.2 aluminum alloy melt, making it react in-situ with Zr introduced during the microalloying of the A356.2 aluminum alloy melt to produce a scattered nano-ZrB 2 ceramic reinforcement, wherein a size of the ZrB 2 is 15-75 nm, and a content of the ZrB 2 is 2.57-5.14 wt. %.