Methods for the production of high solids nanocellulose
The present invention provides, among other things, methods including the steps of providing a cellulosic biomass, associating the cellulosic biomass with an organic liquid to form a mixture, treating the mixture to reduce the moisture content of the mixture to 30% or below (if necessary), and processing the mixture to produce cellulose nanofibrils in a slurry. In some embodiments, provided methods allow for the production of high solids content slurries containing 4% or more cellulosic nanofibrils.
1. A method of producing a nanocellulose composite, the method comprising the steps of:
(a) providing a cellulosic biomass, wherein the cellulosic biomass has a water content less than 30%;
(b) associating the cellulosic biomass with a first organic liquid to form a first mixture, wherein the first organic liquid has a boiling temperature greater than 100° C., and wherein the first organic liquid comprises a monomer;
(c) removing substantially all water from the first mixture;
(d) processing the first mixture to produce a slurry comprising cellulose nanofibrils and the first organic liquid;
(e) heating the first mixture to a temperature at or above the boiling temperature of the first organic liquid; and
(f) polymerizing the slurry,
thereby producing a nanocellulose composite comprising cellulose nanofibrils substantially homogenously distributed in a polymeric compound, wherein no exogenous water is added during the process after the initiation of step (b).
2. The method of claim 1 , wherein the first organic liquid is or comprises lactic acid, propylene glycol, succinic acid, ethylene glycol, dipropylene glycol, 1,3, propanediol, a diol type monomer, a diacid type monomer, a diamine type monomer and combinations thereof.
3. The method of claim 1 , wherein the cellulose nanofibrils comprise at least 4 wt % of the slurry.
4. The method of claim 1 , wherein the polymerization is selected from the group consisting of free radical polymerization, addition or chain growth polymerization, coordination polymerization, condensation or step growth polymerization, and copolymerization.
5. The method of claim 1 , wherein the slurry includes one or more additives.
6. The method of claim 5 , wherein the additive is or comprises a catalyst and/or initiator.
7. A high solids nanocellulose composite produced according to the method of claim 1 .
8. A method of producing a nanocellulose composite, the method comprising the steps of:
(a) providing a cellulosic biomass, wherein the cellulosic biomass has a water content less than 30%;
(b) associating the cellulosic biomass with a first organic liquid to form a first mixture, wherein the first organic liquid has a boiling temperature greater than 100° C., and wherein the first organic liquid comprises a monomer;
(c) removing substantially all water from the first mixture;
(d) processing the first mixture to produce a slurry comprising cellulose nanofibrils and the first organic liquid;
(e) heating the first mixture to a temperature at or above the boiling temperature of the first organic liquid; and
(f) associating the slurry with a second organic liquid to form a high solids nanocellulosic slurry; and
(g) polymerizing the high solids nanocellulosic slurry,
thereby producing a nanocellulose composite comprising cellulose nanofibrils substantially homogenously distributed in a polymeric compound, wherein no exogenous water is added during the process after the initiation of step (b).
9. The method of claim 8 , wherein at least 10% of the first organic liquid is removed from the slurry before association with the second organic liquid.
10. The method of claim 8 , further comprising filtering the high solids nanocellulosic slurry.
11. The method of claim 8 , wherein the second organic liquid has a boiling point at least 3° C. lower than the first organic liquid.
12. The method of claim 8 , wherein the second organic liquid is or comprises ethanol, methanol, isopropanol, n-butanol, formaldehyde, acetaldehyde, acetone, ethyl acetate, acetonitrile, and combinations thereof.
13. The method of claim 8 , wherein the boiling point of the second organic liquid is at least 5° C. lower than the first organic liquid.
14. The method of claim 9 , wherein the removing step results in removal of at least 90% of first organic liquid.
15. The method of claim 9 , wherein the removing and second associating steps are repeated at least once.
16. The method of claim 15 , wherein at least 90% of the first organic liquid is removed.
17. The method of claim 8 , wherein the high solids nanocellulosic slurry comprises at least 4 wt % cellulosic solids.
18. The method of claim 8 , wherein the polymerization is selected from the group consisting of free radical polymerization, addition or chain growth polymerization, coordination polymerization, condensation or step growth polymerization, and copolymerization.
19. The method of claim 8 , wherein the slurry includes one or more additives.
20. The method of claim 19 , wherein the additive is or comprises a catalyst and/or initiator.
21. A high solids nanocellulose composite produced according to the method of claim 8 .