Ion assisted deposition for rare-earth oxide based thin film coatings on process rings
A ring shaped body includes a top flat region, a ring inner side and a ring outer side. The ring inner side comprises an approximately vertical wall. A conformal protective layer is disposed on at least the top flat region, the ring inner side and the ring outer side of the ring shaped body. The protective layer has a first thickness of less than 300 μm on the top flat region and a second thickness on the vertical wall of the ring inner side, where the second thickness is 45-70% of the first thickness.
1. A chamber component for a processing chamber comprising:
a ring shaped body defined by an inner diameter and an outer diameter, the ring shaped body comprising at least one of an oxide based ceramic, a nitride based ceramic or a carbide based ceramic, wherein the ring shaped body is a sintered ceramic body comprising a top flat region, a ring inner side along the inner diameter of the ring shaped body and a ring outer side along the outer diameter of the ring shaped body, wherein the ring inner side comprises an approximately vertical wall and a step on a plasma-facing surface of the ring shaped body; and
a protective layer on at least the top flat region, the ring inner side and the ring outer side of the ring shaped body, wherein the protective layer is a conformal layer comprising a plasma resistant rare earth oxide, has a porosity of less than 1%, has an average surface roughness of less than 6 micro-inches, and has a first thickness of less than 300 μm on the top flat region and a second thickness on the approximately vertical wall of the ring inner side, wherein the second thickness is 45-70% of the first thickness, and wherein the protective layer comprises a composition of 40-45 mol % of Y 2 O 3 , 5-10 mol % of ZrO 2 , 35-40 mol % of Er 2 O 3 , 5-10 mol % of Gd 2 O 3 , and 5-15 mol % of SiO 2 .
2. The chamber component of claim 1 , wherein the protective layer has a thickness of 5-15 μm.
3. The chamber component of claim 1 , wherein a porosity of the protective layer is below 0.1%.
4. The chamber component of claim 1 , wherein the protective layer comprises a protective layer stack comprising a first plasma resistant rare earth oxide film on the ring shaped body and a second plasma resistant rare earth oxide film on the first plasma resistant rare earth oxide film.
5. The chamber component of claim 4 , wherein the first plasma resistant rare earth oxide film comprises a coloring agent that causes the first plasma resistant rare earth oxide film to have a different color than the second plasma resistant rare earth oxide film.
6. The chamber component of claim 5 , wherein the coloring agent comprises at least one of Nd 2 O 3 , Sm 2 O 3 or Er 2 O 3 .
7. The chamber component of claim 5 , wherein the first plasma resistant rare earth oxide film is an amorphous layer comprising Y 3 Al 5 O 12 or Er 3 Al 5 O 12 and the second plasma resistant rare earth oxide film is a crystalline or polycrystalline layer comprising Er 2 O 3 or a ceramic compound comprising Y 4 Al 2 O 9 and a solid-solution of Y 2 O 3 —ZrO 2 .
8. The chamber component of claim 1 , wherein the chamber component is usable at a temperature of 300° C. without causing cracking of the protective layer.
9. The chamber component of claim 1 , further comprising: a transition layer between the ring shaped body and the protective layer, wherein the transition layer is a non-porous layer formed from interdiffusion of material from the ring shaped body and the protective layer.
10. The chamber component of claim 1 , wherein the ring outer side is rounded.
11. A chamber component, comprising:
a ring shaped body defined by an inner diameter and an outer diameter, the ring shaped body comprising at least one of an oxide based ceramic, a nitride based ceramic or a carbide based ceramic, wherein the ring shaped body is a sintered ceramic body comprising a top flat region, a ring inner side along the inner diameter of the ring shaped body and a ring outer side along the outer diameter of the ring shaped body, wherein the ring inner side comprises a step and an approximately vertical wall and a step on a plasma-facing surface of the ring shaped body; and
a protective layer on at least the top flat region, the ring inner side and the ring outer side of the ring shaped body, wherein the protective layer is a conformal layer, has a porosity of less than 1%, has an average surface roughness of less than 6 micro-inches, comprises at least one plasma resistant rare earth oxide film, and has a first thickness of less than 300 μm on the top flat region and the step of the ring inner side and a second thickness on the approximately vertical wall of the ring inner side, wherein the second thickness is 45-70% of the first thickness, and wherein the protective layer comprises a composition of 40-45 mol % of Y 2 O 3 , 5-10 mol % of ZrO 2 , 35-40 mol % of Er 2 O 3 , 5-10 mol % of Gd 2 O 3 , and 5-15 mol % of SiO 2 .