Coated nickel hydroxide powder for alkali secondary battery positive electrode active material and method of producing same
A coated nickel hydroxide powder that has improved dispersibility in a paste to inhibit agglomeration and can be densely packed in a three-dimensional metal porous body in the preparation of a positive electrode for alkaline secondary battery includes nickel hydroxide particles and a coating layer made of a cobalt compound and formed on a surface of the nickel hydroxide particles, wherein when 10 mL of water is added to 10 g of the coated nickel hydroxide powder to prepare a suspension, a total amount of eluted ions except for oxonium ions, hydroxide ions, and carbonate ions in the suspension is 6.5 mmol/L or less. The coated nickel hydroxide powder obtained through a crystallization step, a coating step, and a washing step is dried in a drying step in a decarbonated atmosphere whose partial pressure of a carbon-containing gas is 15 Pa or less.
1. A method for producing a coated nickel hydroxide powder having a total carbon content of 1000 ppm by mass or less for an alkaline secondary battery positive electrode active material, the method comprising:
a crystallization step in which an aqueous alkali solution is supplied to a nickel-containing aqueous solution to obtain nickel hydroxide particles crystallized out by neutralization as core particles;
a coating step in which a coating layer consisting of a cobalt compound is formed on a surface of the core particles to obtain a coated nickel hydroxide powder;
a washing step in which the coated nickel hydroxide powder is washed; and
a drying step in which the coated nickel hydroxide powder after washing is dried,
wherein in the drying step, the coated nickel hydroxide powder is dried in a decarbonated air atmosphere whose partial pressure of a carbon-containing gas is 15 Pa or less.
2. The method for producing a coated nickel hydroxide powder for an alkaline secondary battery positive electrode active material according to claim 1 , wherein in the drying step, the coated nickel hydroxide powder is dried in a decarbonated air atmosphere whose partial pressure of carbon dioxide is 10 Pa or less.
3. The method for producing a coated nickel hydroxide powder according to claim 1 , wherein the drying step is carried out at about 105° C.