Electrolyte for battery containing an iron electrode
Provided is a battery comprising an iron electrode and an electrolyte comprised of sodium hydroxide, lithium hydroxide and a soluble metal sulfide. In one embodiment, the concentration of sodium hydroxide in the electrolyte ranges from 6.0 M to 7.5 M, the amount of lithium hydroxide present in the electrolyte ranges from 0.5 M to 2.0 M, and the amount of metal sulfide present in the electrolyte ranges from 1 to 2% by weight.
1. A battery comprising an iron anode comprised of a single, coated conductive substrate, and an electrolyte comprised of sodium hydroxide, lithium hydroxide and a soluble metal sulfide, wherein the amount of sulfide contained in the electrolyte ranges from 0.23% to 0.75% by weight of the electrolyte, and with the iron electrode comprising a polyvinyl alcohol binder.
2. The battery of claim 1 , wherein the metal sulfide is an alkali metal sulfide.
3. The battery of claim 2 , wherein the metal sulfide is sodium sulfide.
4. The battery of claim 1 , wherein the iron electrode contains sulfur or sulfur compounds.
5. The battery of claim 1 , wherein the battery further comprises a manganese electrode.
6. The battery of claim 1 , wherein the battery is an air battery.
7. The battery of claim 1 , wherein the concentration of sodium hydroxide in the electrolyte is in the range of from 6.0 M to 7.5 M.
8. The battery of claim 1 , wherein the amount of lithium hydroxide in the electrolyte is in the range of from 0.5 to 2.0 M.
9. The battery of claim 1 , wherein the amount of metal sulfide in the electrolyte is in the range of from 1 to 2 M.
10. The battery of claim 1 , wherein the concentration of sodium hydroxide in the electrolyte ranges from 6.0 M to 7.5 M, the amount of lithium hydroxide present in the electrolyte ranges from 0.5 M to 2.0 M, and the amount of metal sulfide present in the electrolyte ranges from 1 to 2% by weight.
11. The battery of claim 10 , wherein the concentration of sodium hydroxide in the electrolyte ranges from 6.0 M to 7.0 M, the amount of lithium hydroxide present in the electrolyte ranges from 0.5 M. to 1.5 M, and the amount of metal sulfide present in the electrolyte ranges from 1 to 1.5 wt %.
12. The battery of claim 10 , wherein the concentration of sodium hydroxide in the electrolyte is about 6.0 M, the concentrates of lithium hydroxide in the electrolyte is about 1.0 M, and the amount of metal sulfide in the electrolyte is about 1% by weight.
13. The battery of claim 1 , wherein the iron electrode is affixed to a two dimensional conductive substrate.
14. The battery of claim 13 , wherein the conductive substrate is a perforated strip or expanded metal.
15. The battery of claim 1 , wherein the iron electrode comprises a three dimensional conductive substrate.
16. The battery of claim 15 , wherein the conductive substrate is a metal foam, metal felt, or metal foil.
17. The battery of claim 16 , wherein the foil is a perforated foil in which the perforation result in burrs that protrude above and below the surface of the foil.
18. The battery of claim 16 , wherein the foil has metallic nickel or iron particles sintered onto the surface of the foil.