Composite resin composition
Provided is a composite resin composition to be used as a material for a molded article produced by a molding machine. The composite resin composition includes a main ingredient resin 1 and a fibrous filler 2 , and the fiber length direction end of the fibrous filler 2 is defibrated. The length of the defibrated portion 3 is 5% or more and 50% or less of the fiber length of the entire fibrous filler 2 . The fiber diameter in the defibrated portion 3 of the fibrous filler 2 is 1/1000 or more and 1/10 or less the fiber diameter in the undefibrated portion. The modulus of elasticity of the fibrous filler 2 is higher than the modulus of elasticity of the main ingredient resin 1 , and the difference between these moduli of elasticity is within 20 GPa.
1. A composite resin composition suitable as a raw material for a molded article produced by a molding machine, and comprising a matrix resin and a fibrous filler,
wherein the fiber length direction end of the fibrous filler is defibrated;
the length of the defibrated portion is 5% or more and 50% or less of the fiber length of the entire fibrous filler;
the fiber diameter in the defibrated portion of the fibrous filler is 1/1000 or more and 1/10 or less the fiber diameter in the undefibrated portion;
the modulus of elasticity of the fibrous filler is higher than the modulus of elasticity of the matrix resin, and the difference between these moduli of elasticity is within 20 GPa, and
voids are present in the composite resin composition at an interface between the resin and the fibrous filler, and the volume of the voids is 3% or more and 10% or less of the volume of the fibrous filler.
2. The composite resin composition according to claim 1 , wherein the fibrous filler is a natural fiber made of cellulose.
3. The composite resin composition according to claim 1 , wherein the matrix resin is an olefin resin.
4. A pellet comprising the composite resin composition according to claim 1 .
5. The pellet according to claim 4 , wherein the fibrous filler partially protrudes from the surface of the pellet.
6. The pellet according to claim 4 , wherein at least either one of the end faces thereof shows an elliptical shape.
7. The composite resin composition according to claim 1 , wherein the voids are present in an amount sufficient to provide increased impact resistance for the composition relative to a composition where the voids are absent.
8. The composite resin composition according to claim 1 , wherein the fibrous filler is obtained from hemp or softwood.