Method of nitriding and inspecting laser-irradiated nickel film
A method of inspection of a laser-irradiated nickel film is disclosed. The method may include: reducing a surface of the laser-irradiated nickel film under a reducing gas atmosphere; heating the surface of the nickel film at 250 degrees Celsius or higher under a nitrogen atmosphere after the reducing; measuring a color of the surface of the nickel film after the heating; and assessing a condition of the surface of the nickel film based on a result of the color measuring.
1. A method of inspection of a laser-irradiated nickel film, the method comprising:
reducing a surface of the laser-irradiated nickel film under a reducing gas atmosphere;
heating the surface of the nickel film at 250 degrees Celsius or higher under a nitrogen atmosphere after the reducing;
measuring a color of the surface of the nickel film after the heating; and
assessing a condition of the surface of the nickel film based on a result of the color measuring.
2. The method according to claim 1 , wherein
the result of the color measuring comprises at least an index indicating a blue component, and
the assessing of the condition comprises assessing the condition of the surface of the nickel film based on the index indicating the blue component.
3. The method according to claim 2 , wherein
the assessing of the condition comprises assessing cleanliness of the nickel film based on the index indicating the blue component.
4. The method according to claim 3 , wherein
the assessing of the condition comprises assessing whether an organic compound adheres to the nickel film or not based on the index indicating the blue component.
5. The method according to claim 4 , wherein
the assessing of the condition comprises assessing that the organic compound adheres to the nickel film when the index indicating the blue component is greater than a predetermined reference value.
6. The method according to claim 2 , wherein
the assessing of the condition comprises assessing a processed condition of the nickel film created by the laser irradiation based on the index indicating the blue component.
7. The method according to claim 6 , wherein
the assessing of the condition comprises assessing that the processed condition of the nickel film created by the laser irradiation is defective when the index indicating the blue component is greater than a predetermined reference value.
8. The method according to claim 1 , wherein
the result of the color measuring comprises at least an index indicating a red component, and
the assessing of the condition comprises assessing the condition of the surface of the nickel film based on the index indicating the red component.
9. The method according to claim 8 , wherein
the assessing of the condition comprises assessing a processed condition of the nickel film created by the laser irradiation based on the index indicating the red component.
10. The method according to claim 9 , wherein
the assessing of the condition comprises assessing that the processed condition of the nickel film created by the laser irradiation is defective when the index indicating the red component is less than a predetermined reference value.