Multilayer ceramic electronic component having improved internal electrode, and method of manufacturing the same

1. A method of manufacturing a multilayer ceramic electronic component, the method comprising:

preparing a ceramic green sheet;

forming an internal electrode pattern by coating a paste for an internal electrode including conductive powder including tin (Sn) on the ceramic green sheet;

forming a ceramic multilayer structure by stacking the ceramic green sheets on which the internal electrode pattern is formed; and

forming a body including a dielectric layer and an internal electrode by sintering the ceramic multilayer structure,

wherein a content of tin (Sn) is greater than or equal to about 1.5 wt %, based on a total weight of the conductive powder, and

wherein a metal coating layer including tin (Sn) is formed on a surface of the conductive powder.

2. The method of claim 1 , wherein the ceramic green sheet has a thickness equal to or less than 0.6 μm and the internal electrode pattern has a thickness equal to or less than 0.5 μm.

3. The method of claim 1 , wherein the metal coating layer further includes at least one selected from the group of copper (Cu), silver (Ag), palladium (Pd), platinum (Pt), rhodium (Rh), iridium (Ir), and ruthenium (Ru).

4. The method of claim 1 , wherein the metal coating layer further includes at least one selected from the group of tungsten (W), molybdenum (Mo), chromium (Cr), and cobalt (Co).

5. The method of claim 1 , wherein the metal coating layer is formed using an atomic layer deposition (ALD) process.

6. The method of claim 1 , wherein the conductive powder includes an alloy of tin (Sn), and the alloy further include at least one selected from the group of copper (Cu), silver (Ag), palladium (Pd), platinum (Pt), rhodium (Rh), iridium (Ir), and ruthenium (Ru).

7. The method of claim 1 , wherein the conductive powder includes an alloy of tin (Sn), and the alloy further includes at least one selected from the group of tungsten (W), molybdenum (Mo), chromium (Cr), and cobalt (Co).

8. The method of claim 1 , wherein the conductive powder further includes sulfur (S) in a content of 300 ppm or less, based on a total content of the conductive powder.

9. The method of claim 1 , wherein the conductive powder is nickel (Ni) powder.

10. The method of claim 1 , wherein the body has a length equal to or less than 0.4 mm and a thickness equal to or less than 0.2 mm.

11. A multilayer ceramic electronic component manufactured using the method of claim 1 , comprising:

the body including the dielectric layer and the internal electrode; and

an external electrode disposed on the body,

wherein the internal electrode includes a metallic crystal grain and a metal composite layer surrounding the metallic crystal grain and including nickel (Ni) and tin (Sn).

12. The multilayer ceramic electronic component of claim 11 , wherein the dielectric layer has a thickness equal to or less than 0.4 μm and the internal electrode has a thickness equal to or less than 0.4 μm.

13. The multilayer ceramic electronic component of claim 11 , wherein the metal composite layer including nickel (Ni) and tin (Sn) has a thickness within a range from 1 to 15 nm.

14. The multilayer ceramic electronic component of claim 11 , wherein the metallic crystal grain is a nickel (Ni) crystal grain.

15. The multilayer ceramic electronic component of claim 11 , wherein 85%≤C, where C is a ratio of a length of portions on which the internal electrode is actually formed to an entire length of the internal electrode.

16. The multilayer ceramic electronic component of claim 11 , wherein the metallic crystal grain includes a nickel (Ni) crystal grain, and

wherein the metal composite layer including tin (Sn) and nickel (Ni) substantially surrounds the nickel (Ni) crystal grain.

17. A multilayer ceramic electronic component, comprising:

a body including a dielectric layer and an internal electrode; and

an external electrode disposed on the body and connected to the internal electrode,

wherein the internal electrode includes nickel (Ni) and a metal composite layer including nickel (Ni) and tin (Sn), and

wherein, in the internal electrode, a content of tin (Sn) is greater than or equal to about 1.5 wt %, based on a total weight of the internal electrode.

18. The multilayer ceramic electronic component of claim 17 , wherein the metal composite layer further includes at least one selected from the group of copper (Cu), silver (Ag), palladium (Pd), platinum (Pt), rhodium (Rh), iridium (Ir), and ruthenium (Ru).

19. The multilayer ceramic electronic component of claim 17 , wherein the metal composite layer further includes at least one selected from the group of tungsten (W), molybdenum (Mo), chromium (Cr), and cobalt (Co).

20. The multilayer ceramic electronic component of claim 17 , wherein the internal electrode further includes sulfur (S) in a content of 300 ppm or less, based on a total content of conductive powder.

21. A method of manufacturing a multilayer ceramic electronic component, the method comprising:

preparing a ceramic green sheet;

forming an internal electrode pattern by coating a paste for an internal electrode including conductive powder including tin (Sn) on the ceramic green sheet;

forming a ceramic multilayer structure by stacking the ceramic green sheets on which the internal electrode pattern is formed; and

forming a body including a dielectric layer and an internal electrode by sintering the ceramic multilayer structure,

wherein a content of tin (Sn) is greater than or equal to about 1.5 wt %, based on a total weight of the conductive powder, and

wherein a coating layer including tin (Sn) is formed on a surface of the conductive powder using an atomic layer deposition (ALD) process.