Modified polyethylene resins and method for making the same
A method for increasing the melt strength and/or low shear viscosity of a polyethylene resin, the method comprising: a) providing a first polyethylene resin having a density ranging from 0.900 g/cm 3 to 0.970 g/cm 3 , a melt index ranging from 0.01 g/10 min to 30 g/10 min, and at least 0.20 vinyl groups per 1,000 total carbons; b) providing a masterbatch composition comprising a free radical generator and a second polyethylene resin, wherein the free radical generator has a half-life at 220° C. of less than 200 seconds, and a decomposition energy higher than −250 kJ/mol, and wherein the second polyethylene resin has a density ranging from 0.900 g/cm 3 to 0.970 g/cm 3 , melt index ranging from 0.01 g/10 min to 100 g/10 min; and c) reacting the first polyethylene resin with the masterbatch composition to form a modified polyethylene resin.
1. A method for increasing the melt strength and/or low shear viscosity of a polyethylene resin, the method comprising:
a) providing a first polyethylene resin having a density ranging from 0.900 g/cm 3 to 0.970 g/cm 3 , a melt index, (I 2 ), ranging from 0.01 g/10 min to 30 g/10 min, and at least 0.20 vinyl groups per 1,000 total carbons;
b) providing a masterbatch composition comprising a free radical generator and a second polyethylene resin, wherein the free radical generator has a half-life at 220° C. of less than 200 seconds, and a decomposition energy higher than −250 kJ/mol, and wherein the second polyethylene resin has a density ranging from 0.900 g/cm 3 to 0.970 g/cm 3 , and melt index, (I 2 ), ranging from 0.01 g/10 min to 100 g/10 min; and
c) reacting the first polyethylene resin with the masterbatch composition to form a modified polyethylene resin.
2. The method of claim 1 , wherein the amount of free radical generator is less than 30 ppm relative to the total amount of resin.
3. The method of claim 1 , wherein the free radical generator has a half-life at 220° C. of between 60 seconds and 120 seconds.
4. The method of claim 1 , wherein the masterbatch composition comprises less than 1,000 ppm of primary antioxidant.
5. The method of claim 1 , wherein the first polyethylene resin comprises less than 2,000 ppm primary antioxidant.
6. The method of claim 1 , wherein the first polyethylene resin comprises less than 250 ppm of primary antioxidant and the second polyethylene resin comprises less than 250 ppm of primary antioxidant.
7. The method of claim 1 , wherein the molecular weight of the free radical generator is from 200-1,000 Daltons.
8. The method of claim 1 , wherein the free radical generator is a cyclic peroxide.
9. The method of claim 1 , wherein the reacting of the first polyethylene resin with the free radical generator takes place in an extruder.
10. A composition formed from the modified polyethylene resin obtained from the method of claim 1 .
11. A film formed from the modified polyethylene resin obtained from the method of claim 1 .
12. The film of claim 11 , wherein the film is a blown film.
13. The film of claim 11 , wherein the film is a cast film.
14. The film of claim 11 , wherein the film is a multilayer film.
15. The film of claim 11 , wherein the film is a monolayer film.