Use of a bifunctional catalyst based on IZM-2 with a specific Si/Al ratio for the isomerization of long paraffinic feedstocks to middle distillates
The present invention describes a process for the isomerization of paraffinic feedstocks operating at a temperature of between 200° C. and 500° C., at a total pressure of between 0.45 MPa and 7 MPa, at a hydrogen partial pressure of between 0.3 and 5.5 MPa, at an hourly space velocity of between 0.1 and 10 kilograms of feedstock introduced per kilogram of catalyst and per hour and using a catalyst comprising at least one metal of group VIII of the periodic table of elements, at least one matrix and at least one zeolite IZM-2, in which the ratio between the number of moles of silicon and the number of moles of aluminium of the zeolite IZM-2 network is between 25 and 55, preferably between 25 and 50, and preferably between 30 and 50.
1. Process for isomerization of a paraffinic feedstock having between 9 and 25 carbon atoms, said paraffinic feedstock been produced from renewable resources selected from plant oils, oils of algae or algal oils, fish oils and fats of plant or animal origin, or mixtures thereof, or by a process comprising upgrading the paraffinic feedstock via a Fischer-Tropsch route,
wherein the isomerization process operates at a temperature of between 200° C. and 500° C., at a total pressure of between 0.45 MPa and 7 MPa, at a hydrogen partial pressure of between 0.3 and 5.5 MPa, at an hourly space velocity of between 0.1 and 10 kilograms of paraffinic feedstock introduced per kilogram of catalyst and per hour and with a catalyst comprising at least one metal of group VIII of the periodic table of elements, at least one matrix and a IZM-2 zeolite,
wherein a molar ratio of silicon to network aluminium of the IZM-2 zeolite is between 25 and 55.
2. Process according to claim 1 , in which the molar ratio of silicon to network aluminium of the IZM-2 zeolite is between 25 and 50.
3. Process according to claim 1 , in which the molar ratio of silicon to network aluminium of the IZM-2 zeolite is between 30 and 50.
4. Process according to claim 1 , in which said matrix is aluminates or said matrix is selected from alumina, silica, silica-alumina, clays, titanium oxide, boron oxide, zirconia, and mixtures thereof.
5. Process according to claim 1 , in which the metal of group VIII is selected from iron, cobalt, nickel, ruthenium, rhodium, palladium, osmium, iridium and platinum.
6. Process according to claim 5 , in which the metal of group VIII is selected from the noble metals of group VIII.
7. Process according to claim 6 , in which the noble metal content of said catalyst is between 0.01% and 5% by weight relative to the total weight of said catalyst.
8. Process according to claim 6 , wherein the metal from said noble metals of group VIII is selected from palladium and platinum.
9. Process according to claim 1 , comprising at least one additional metal selected from metals of groups IIIA, IVA and VIIB of the periodic table of elements.
10. Process according to claim 9 wherein the metals of groups IIIA, IVA and VIIB of the periodic table of elements are selected from gallium, indium, tin and rhenium.
11. Process according to claim 1 , in which said process is carried out at a temperature of between 200° C. and 450° C., at a total pressure of between 0.6 MPa and 6 MPa, at a hydrogen partial pressure of between 0.4 and 4.8 MPa, and at an hourly space velocity of between 0.2 and 7 kilograms of feedstock introduced per kilogram of catalyst and per hour.