Block copolymer ink formulation for 3D printing and method of making a 3D printed radiofrequency (RF) device

1. A 3D printed radiofrequency (RF) device comprising:

a printed dielectric body comprising a triblock copolymer including end blocks comprising an aromatic or acrylate polymer and a midblock between the end blocks comprising an aliphatic polymer,

wherein the printed dielectric body is a composite body comprising the triblock copolymer as a matrix and further comprising a plurality of dielectric filler particles dispersed therein; and

wherein the printed dielectric body exhibits a dielectric loss tangent ε″/ε′ of less than about 0.005.

2. The 3D printed RF device of claim 1 , wherein the printed dielectric body exhibits at least one of an average surface roughness of about 2 microns or less and a dielectric constant (ε′) greater than 2.

3. The 3D printed RF device of claim 1 , wherein the end blocks of the triblock copolymer comprise polystyrene and/or a derivative of polystyrene;

wherein the midblock of the triblock copolymer comprises polybutadiene, polyisoprene, poly(ethylene-ran-butylene), a polybutadiene derivative, a polyisoprene derivative, or a poly(ethylene-ran-butylene) derivative.

4. The 3D printed RF device of claim 1 ,

wherein the dielectric filler particles are present at a concentration of at least about 20 wt. %.

5. The 3D printed RF device of claim 1 , wherein the RF device operates in the Ka band and is selected from the group consisting of: filter,

antenna, lens, radome, horn, transducer and transition.

6. The 3D printed RF device of claim 1 , wherein the dielectric filler particles are present at a concentration of at least 40 wt. %.

7. The 3D printed RF device of claim 1 , wherein the dielectric filler particles are present at a concentration of at least 60 wt. %.

8. The 3D printed RF device of claim 1 , wherein the dielectric filler particles comprise at least one dielectric material selected from the group consisting of aluminum oxide, boron nitride, beryllium oxide, magnesium oxide, magnesium titanate, titanium dioxide, strontium titanate, barium titanate, molybdenum sulfide, zinc oxide, magnesium carbonate, borosilicate glass, mica, sapphire, fused silica, fused quartz, steatite, soda-line glass, zirconia, and wollastonite.

9. The 3D printed RF device of claim 1 , wherein the dielectric filler particles comprise at least one dielectric material selected from the group consisting of magnesium oxide, aluminum oxide, titanium dioxide and strontium titanate.

10. The 3D printed RF device of claim 9 , wherein the dielectric filler particles comprise magnesium oxide.

11. The 3D printed RF device of claim 9 , wherein the dielectric filler particles comprise aluminum oxide.

12. The 3D printed RF device of claim 9 , wherein the dielectric filler particles comprise titanium dioxide.

13. The 3D printed RF device of claim 9 , wherein the dielectric filler particles comprise strontium titanate.

14. The 3D printed RF device of claim 1 , wherein the dielectric filler particles have an average particle size in the range from about 1 nanometer to about 10 microns.

15. The 3D printed RF device of claim 1 , wherein the dielectric filler particles have an average particle size in the range from about 5 nanometers to about 500 nanometers.

16. The 3D printed RF device of claim 1 , wherein the dielectric filler particles are surface-modified to increase compatibility with the triblock copolymer.

17. The 3D printed RF device of claim 1 , wherein the dielectric filler particles are modified by applying a hydrophobic moiety to the surfaces of the particles.

18. The 3D printed RF device of claim 17 , wherein the hydrophobic moiety applied to the surfaces of the particles is moiety selected from the group of titanate, zirconate, aluminate and silane coupling agents and surfactants.

19. A method of making the 3D printed radiofrequency (RF) device of claim 1 , the method comprising:

extruding an ink formulation from a deposition nozzle moving relative to a substrate, the ink formulation comprising a triblock copolymer in a solvent, the triblock copolymer including end blocks comprising an aromatic or acrylate polymer and a midblock between the end blocks comprising an aliphatic polymer; and

depositing one or more continuous filaments comprising the ink formulation in a predetermined pattern on the substrate; and

treating the ink formulation to remove or cure the solvent, thereby forming a printed RF device.

20. The method of claim 19 , wherein the treating of the ink formulation entails drying, heating and/or exposure to UV radiation.

21. The method of claim 19 , wherein the end blocks of the triblock copolymer include an aromatic polymer comprising polystyrene and/or a derivative of polystyrene,

wherein the midblock of the triblock copolymer comprises polybutadiene, polyisoprene, poly(ethylene-ran-butylene), a polybutadiene derivative, a polyisoprene derivative, or a poly(ethylene-ran-butylene) derivative.

22. The method of claim 19 , wherein the triblock copolymer is present at a concentration of at least about 40 wt. %.

23. The method of claim 19 , wherein the ink formulation further comprises a plurality of dielectric filler particles;

wherein the dielectric filler particles are present at a concentration of at least about 20 wt. % and the triblock copolymer is present at a concentration of at least about 20 wt. %.

24. The method of claim 19 , wherein the solvent comprises an aromatic solvent, a vinyl-containing monomer, or a combination thereof.

25. The method of claim 19 , wherein the RF device operates in the Ka band and is selected from the group consisting of: filter, antenna, lens, radome, horn, transducer and transition.