Interlayer film for laminated glass and laminated glass

1. An interlayer film, comprising at least one layer A containing a thermoplastic elastomer, wherein

the shear storage modulus of the layer A at 70° C. as measured by performing a dynamic viscoelasticity test at a frequency of 1,000 Hz in accordance with ASTM D4065-06 is 1 MPa or more, and a layer having a higher shear storage modulus than the layer A is provided on at least one surface of the layer A,

a UV absorber is contained in at least the layer A, the area density (g/m 2 ) of the UV absorber in the layer A is 0.1 or more and 8 or less, and

at least one surface of the interlayer film is in a state of having been shaped.

2. The interlayer film according to claim 1 , wherein the elastic limit of the layer A at 20° C. is 4 N or more.

3. The interlayer film according to claim 1 , wherein the height of an embossed portion of the shaped surface is from 10 to 150 μm.

4. The interlayer film according to claim 1 , wherein the peak maximum in tan δ as measured for the layer A by performing a dynamic viscoelasticity test at a frequency of 1,000 Hz in accordance with ASTM D4065-06 appears in the range of −10 to 30° C.

5. The interlayer film according to claim 1 , wherein the height of the peak maximum in tan δ as measured for the layer A by performing a dynamic viscoelasticity test at a frequency of 1,000 Hz in accordance with ASTM D4065-06 is 1.3 or more.

6. The interlayer film according to claim 1 , wherein as the layer having a higher shear storage modulus than the layer A, a layer B containing a thermoplastic resin is provided.

7. The interlayer film according to claim 6 , wherein the content of a plasticizer in the layer B is 50 parts by mass or less with respect to 100 parts by mass of the thermoplastic resin.

8. The interlayer film according to claim 6 , wherein the thermoplastic resin in the layer B is a polyvinyl acetal resin.

9. The interlayer film according to claim 6 , wherein the thermoplastic resin in the layer B is an ionomer resin.

10. The interlayer film according to claim 1 , wherein a laminated glass in which the interlayer film is sandwiched between two glasses with the total thickness of the glasses being 4 mm or less has a sound transmission loss at 4,000 Hz as measured under the conditions of ASTM E 90-09 of 37 dB or more.

11. The interlayer film according to claim 1 , wherein the thermoplastic elastomer is composed of a hard segment block and a soft segment block, and the hard segment block is a polystyrene block or a polymethyl methacrylate block.

12. The interlayer film according to claim 1 , further comprising a heat shielding material in at least one of the layers constituting the interlayer film.

13. The interlayer film according to claim 1 , wherein a laminated glass in which the interlayer film is sandwiched between two clear glasses with the total thickness of the glasses being 4 mm or less has a visible light transmittance of 70% or more and an average transmittance of infrared light in the wavelength range of 800 to 1,100 nm of 70% or less.

14. The interlayer film according to claim 1 , wherein a laminated glass in which the interlayer film is sandwiched between two green glasses with the total thickness of the glasses being 4 mm or less has a visible light transmittance of 70% or more and an average transmittance of infrared light in the wavelength range of 800 to 1,100 nm of 32% or less.

15. The interlayer film according to claim 1 , further comprising a heat shielding material,

wherein the heat shielding material is at least one material selected from tin-doped indium oxide, antimony-doped tin oxide, zinc antimonate, metal-doped tungsten oxide, a phthalocyanine compound, aluminum-doped zinc oxide, and lanthantum hexaboride.

16. The interlayer film according to claim 1 , wherein the UV absorber is at least one compound selected from the group consisting of a benzotriazole-based compound, a benzophenone-based compound, a triazne-based compound, a benzoate-based compound, a malonic ester-based compound, and an oxalic anilide-based compound.

17. The interlayer film according to claim 1 , wherein a laminated glass in which the interlayer film is sandwiched between two glasses with the total thickness of the glasses being 4 mm or less has a haze of 5 or less.

18. A laminated glass, comprising the interlayer film according to claim 1 disposed between two glasses.

19. An interlayer film, comprising at least comprising at least one layer A containing a thermoplastic elastomer, wherein

the shear storage modulus of the layer A at 70° C. as measured by performing a dynamic viscoelasticity test at a frequency of 1,000 Hz in accordance with ASTM D4065-06 is 1 MPa or more, and a layer having a higher shear storage modulus than the layer A is provided on at least one surface of the layer A,

a UV absorber is contained in at least the layer A, the area density (g/m 2 ) of the UV absorber in the layer A is 0.5 or more and 10.0 or less, and

at least one surface of the interlayer film is in a state of having been shaped.

20. An interlayer film, comprising at least one layer A containing a thermoplastic elastomer, wherein

the interlayer film comprises the layer B containing a thermoplastic resin and having a higher shear storage modulus than the layer A,

a laminated structure of a laminate constituting the interlayer is layer B/layer A/layer B,

the shear storage modulus of the layer A at 70° C. as measured by performing a dynamic viscoelasticity test at a frequency of 1,000 Hz in accordance with ASTM D4065-06 is 1 MPa or more, and a layer having a higher shear storage modulus than the layer A is provided on at least one surface of the layer A, and

both surfaces of the interlayer film is in a state of having been shaped.