Method for manufacturing structure material
A method for manufacturing a structure material is a method for manufacturing a structure material that includes a thermoplastic resin, reinforced fibers, and voids. The method includes: a first process for arranging a structure precursor comprising the thermoplastic resin and the reinforced fibers in a mold with a surface temperature of 80° C. or less; a second process for raising the surface temperature of the mold up to a temperature at which a storage elastic modulus (G′) of the structure precursor is less than 1.2×10 8 Pa; a third process for lowering the surface temperature of the mold down to a temperature at which the storage elastic modulus (G′) of the structure precursor is 1.2×10 8 Pa or more; and a fourth process for removing a structure material obtained after end of the third process from the mold.
1. A method for manufacturing a structure material product that comprises a thermoplastic resin, reinforced fibers, and voids, the method comprising:
a first process step of arranging a structure precursor comprising the thermoplastic resin and the reinforced fibers in a mold with a surface temperature of 80° C. or less, the reinforced fibers inside the structure precursor being in a compressed state;
a second process step of raising the surface temperature of the mold up to a temperature at which a storage elastic modulus (G′) of the structure precursor is less than 1.2×10 8 Pa so as to raise the reinforced fibers in the compressed state to form the voids;
a third process step of lowering the surface temperature of the mold down to a temperature at which the storage elastic modulus (G′) of the structure precursor is 1.2×10 8 Pa or more so as to form the structure material product; and
a fourth process step of removing the structure material product from the mold.
2. The method for manufacturing the structure material product according to claim 1 , wherein a filling rate of the structure precursor in the mold is within a range of 10% or more and 80% or less of a cavity of the mold.
3. The method for manufacturing the structure material product according to claim 1 , wherein a pressurizing force applied by the mold in the second process step and the third process step is within a range of 0 MPa or more and 5 MPa or less.
4. The method for manufacturing the structure material product according to claim 1 , wherein a size of a cavity of the mold does not change before and after molding.
5. The method for manufacturing the structure material product according to claim 1 , further comprising a process step of arranging at least one of a thermosetting resin composition containing a thermosetting resin and a thermoplastic resin composition containing a thermoplastic resin on a surface of the structure precursor or the structure material product.
6. The method for manufacturing the structure material product according to claim 1 , wherein a weight of the mold is 30 kg or less.
7. The method for manufacturing the structure material product according to claim 1 , wherein the structure precursor contains a foaming agent.
8. The method for manufacturing the structure material product according to claim 1 , wherein the structure precursor comprises a mat comprising reinforced fibers and a matrix resin comprising a thermoplastic resin, and the mat comprising reinforced fibers is impregnated with a resin in advance.
9. The method for manufacturing the structure material product according to claim 1 , wherein a mat comprising the reinforced fibers has a nonwoven fabric-like form manufactured by any of a wet paper making method, a dry paper making method, an air-laid method, and a weaving method.
10. The method for manufacturing the structure material product according to claim 1 , wherein a matrix resin in the structure precursor is given in any form of film, particles, fibers, and liquid.
11. The method for manufacturing the structure material product according to claim 1 , wherein the first process step includes a step of arranging the structure precursor made into a rectangular or wound body in the mold.
12. The method for manufacturing the structure material product according to claim 1 , wherein a shape of the mold is cylindrical columnar, polygonal columnar, cylindrical tubular, or polygonal tubular.
13. The method for manufacturing the structure material product according to claim 1 , wherein a pressurizing force applied by the mold in the second process step and the third process step is 0 MPa by using a mold having a cavity with a size that does not change before or after molding.
14. A method for manufacturing a structure material product that comprises a thermosetting resin, reinforced fibers, and voids, the method comprising:
a first process step of arranging a structure precursor comprising the thermosetting resin before setting and the reinforced fibers in a mold with a surface temperature of 80° C. or less, the reinforced fibers inside the structure precursor being in a compressed state;
a second process step of raising the surface temperature of the mold up to a temperature at which a degree of curing of the structure precursor is 10% or more and 90% or less so as to raise the reinforced fibers in the compressed state to form the voids;
a third process step of maintaining the structure precursor shape until the degree of curing of the structure precursor becomes higher than 90% so as to form the structure material product; and
a fourth process step of removing the structure material product from the mold.
15. The method for manufacturing the structure material product according to claim 14 , wherein the structure precursor comprises a mat comprising reinforced fibers and a matrix resin comprising a thermosetting resin, and the mat comprising reinforced fibers is impregnated with a resin in advance.