Sound absorption material preparation method, sound absorption material and filling method thereof
A sound absorption material preparation method, a sound absorption material and a filling method thereof. The preparation method comprises: S1, preparing a non-foaming material slurry; S2, producing a combustible material framework and a cover-shape container, and placing the combustible material framework into the cover-shape container; S3, forming the non-foamed material slurry in the cover-shape container to form a wet formed body; S4, drying the wet formed body to form a dry formed body; and S5, calcining the dry formed body, wherein the combustible material framework is burned off during the calcining step to form connected channels with a three-dimensional structure in the sound absorption material. The preparation method is simple in operation. Connected channels with a three-dimensional structure are formed in the sound absorption material so that the sound absorption effect is improved. The sound absorption material is prepared by the preparation method, has connected channels with a three-dimensional structure therein, and has a good sound absorption effect. The filling method comprises first pre-forming the sound absorption material and then filling same into a space to be filled, so that the sound absorption material fully fills the space to be filled.
1. A sound absorption material preparation method, comprising the following steps:
S1, preparing a non-foamed material slurry, and mixing the slurry uniformly;
S2, producing a combustible material framework and a cover-shaped container according to a set structure, and placing the combustible material framework in the cover-shaped container;
S3, forming the non-foamed material slurry in the cover-shaped container to form a wet formed body, and separating the wet formed body from the cover-shaped container;
S4, drying the wet formed body to form a dry formed body; and
S5, calcining the dried formed body, wherein the combustible material framework is burned off during the calcining step to form connected channels with a three-dimensional structure in the sound absorption material,
wherein:
the connected channels with the three-dimensional structure corresponds to the combustible material framework,
the connected channels with the three-dimensional structure and the combustible material framework have the set structure, and
the connected channels with the three-dimensional structure is formed to propagate a sound air flow.
2. The preparation method of claim 1 , wherein the non-foamed material slurry comprises a non-foamed powder material, a binder and a pore-forming agent.
3. The preparation method of claim 2 , wherein the non-foamed powder material is one or more of natural zeolite powder, white carbon black, activated carbon powder and a molecular sieve.
4. The preparation method of claim 2 , wherein the binder is an organic silicone sol binder.
5. The preparation method of claim 1 , wherein the combustible material framework adopts an activated carbon fiber material.
6. A sound absorption material made of a non-foamed material and having a set space structure in which connected channels with a three-dimensional structure are formed,
wherein the connected channels with the three-dimensional structure corresponds to the set space structure,
wherein the connected channels with the three-dimensional structure has the set space structure, and
wherein the connected channels with the three-dimensional structure is formed to propagate a sound air flow.
7. The sound absorption material of claim 6 , wherein specific surface area and density of the sound absorption material are 150-450 m2/g and 0.3-0.7 g/cm3, respectively.
8. The sound absorption material of claim 6 , wherein pores are formed inside the sound absorption material, pore volume being 0.5-1.7 cm3/g and macropore diameter being 0.1-50 μm.
9. A sound absorption material filling method, comprising the following steps:
SS1, preparing a non-foamed material slurry, and mixing the slurry uniformly;
SS2, producing a combustible material framework and a cover-shaped container according to a structure of a space to be filled, and placing the combustible material framework in the cover-shaped container;
SS3, forming the non-foamed material slurry in the cover-shaped container to form a wet formed body, and separating the wet formed body from the cover-shaped container;
SS4, drying the wet formed body to form a dry formed body;
SS5, calcining the dried formed body to obtain a sound absorption material block capable of filling the space, wherein the combustible material framework is burned off during the calcining step to form connected channels with a three-dimensional structure in the sound absorption material block; and
SS6, filling the sound absorption material block into the space to be filled,
wherein:
the connected channels with the three-dimensional structure corresponds to the combustible material framework,
the connected channels with the three-dimensional structure and the combustible material framework have the structure, and
the connected channels with the three-dimensional structure is formed to propagate a sound air flow.