Lithium recovery from phosphate minerals
A process for the recovery of lithium from minerals rich in lithium and phosphate, the process comprising passing an ore containing one or more minerals rich in lithium and phosphate to an acid leach step thereby producing a pregnant leach solution, subjecting the pregnant leach solution to a series of process steps by which one or more impurity elements are removed, and recovering lithium as a lithium containing salt product, wherein the series of process steps by which one or more impurity elements are removed includes a low pH impurity removal step conducted at an elevated temperature for the precipitation of one or more impurities.
1. A process for the recovery of lithium from minerals rich in lithium and phosphate, the process characterised by comprising
passing an ore containing one or more minerals rich in lithium and phosphate to an acid leach step thereby producing a pregnant leach solution,
subjecting the pregnant leach solution to a series of process steps by which one or more impurity elements are removed, and
recovering lithium as a lithium containing salt product,
wherein the series of process steps by which one or more impurity elements are removed includes a low pH impurity removal step conducted at a pH ranging from 2 to 3 and at an elevated temperature of greater than 90° C. for the precipitation of one or more impurities,
wherein the one or more impurities including alunite, and
wherein a base is added to the low pH impurity removal step.
2. The process of claim 1 , wherein the base added to the low pH impurity removal step is one or more of limestone, lime or monovalent carbonate, or hydroxide salts.
3. The process of claim 1 , wherein the precipitated impurities of the low pH impurity removal step include sulfuric acid, sodium, aluminium, phosphate, and/or fluoride.
4. The process of claim 1 , wherein the conditions of the low pH impurity removal step are such that substantially no lithium is co-precipitated in the low pH impurity removal step.
5. The process of claim 1 , wherein the lithium containing salt product contains Li 2 CO 3 and/or LiOH.H 2 O.
6. The process of claim 1 , the lithium and phosphate rich minerals include amblygonite and/or montebrasite.
7. The process of claim 1 , wherein a pre-treatment step is provided prior to the acid leach step, the pre-treatment step comprising one or both of a concentration step.
8. The process of claim 7 , wherein the milling step produces a product having a particle size of
<P 80 150 micron.
9. The process of claim 1 , wherein concentrated sulfuric acid is added during the acid leach step and results in at least a proportion of any contained lithium, sodium, phosphate, aluminium and fluoride being extracted into solution, thereby forming the pregnant leach solution.
10. The process of claim 1 , wherein the leaching step is conducted under atmospheric pressure conditions and
at a temperature at or about 90 to 120° C.
11. The process of claim 9 , wherein the leaching step is carried out with an excess of H 2 SO 4 providing a free acid concentration of greater than about 50 g/L H 2 SO 4 and:
the total sulfate concentration is 6.0M S at >90° C.
12. The process of claim 1 , wherein in the acid leach step greater than about 90% metal extraction is achieved with a retention time of about 12 hours.
13. The process of claim 1 , wherein the low pH impurity removal step produces precipitated solids that are washed with water to recover entrained lithium.
14. The process of claim 1 , wherein a filtrate is passed from the low pH impurity removal step to a high pH impurity removal step, in which impurity base metals are precipitated through the addition of a base, the base being lime and/or a monovalent hydroxide salt, and the impurity base metals including iron, manganese, and/or magnesium.
15. The process of claim 14 , wherein calcium is precipitated from a filtered product of the high pH impurity removal step by the addition of a monovalent carbonate salt being Li 2 CO 3 or Na 2 CO 3 .
16. The process of claim 14 , wherein calcium is precipitated from a filtered product of the high pH impurity removal step by the addition of a monovalent carbonate salt being Li 2 CO 3 or Na 2 CO 3 , and lithium carbonate is precipitated by the addition of a monovalent carbonate salt to a filtered product of calcium precipitation.
17. The process of claim 14 , wherein the high pH impurity removal step is operated at a pH of >9.
18. The process of claim 1 , wherein a filtrate is passed from the low pH impurity removal step to a high pH impurity removal step, in which impurity base metals are precipitated through the addition of a base,
the base being lime and/or a monovalent hydroxide salt, and
the impurity base metals including iron, manganese, and/or magnesium,
calcium further being precipitated from a filtered product of the high pH impurity removal step by the addition of a monovalent carbonate salt being Li 2 CO 3 or Na 2 CO 3 , and
lithium carbonate is precipitated by the addition of a monovalent carbonate salt to a filtered product of calcium precipitation, the Li 2 CO 3 precipitation stage being operated at an elevated temperature of >90° C., and the liquor volume is reduced by evaporation.
19. The process of claim 18 , wherein the elevated temperature of the Li 2 CO 3 precipitation stage is operated at >90° C.
20. The process of claim 16 , wherein the monovalent carbonate salt is Na 2 CO 3 .