Composition for fire extinguishant
The present composition for extinguishant mainly comprises of composite A and compound B; wherein said Composite A further comprises Compound C or Compound C and e-glass fibre and Compound B is water or deionized water; wherein further, said Compound C is in turn synthetic hydrated calcium silicate of density 60 to 450 kg/m 3 preferably 90 to 400 kg/m 3 ; which includes range of Tobermorite, Xenotlite and Wollastonite; said Compound C contains negligible amounts of Fe 2 O 3 MgO and Al 2 O 3 . Said Composite A comprises of 93-96% Compound C and 7-4% e-glass fibre and Compound B is at room temperature. The wet composition of present composition for extinguishant comprises of 2% to 18% W/V of Composite A in Compound B, and dry composition for extinguishant comprises of Composite A:compound B=82-98%:18-2%.
1. A wet composition for extinguishing fires, comprising:
a composite material comprising a synthetic hydrated calcium silicate; and
water, wherein the wet composition comprises 2% w/v to 18% w/v of the composite material in the water, the composite material has a particle size ranging from greater than zero μm to 72 μm and the synthetic hydrated calcium silicate has a density ranging from 60 kg/m 3 to 450 kg/m 3 .
2. The wet composition of claim 1 , wherein the synthetic hydrated calcium silicate has a density ranging from 90 kg/m 3 to 400 kg/m 3 .
3. The wet composition of claim 1 , wherein the synthetic hydrated calcium silicate comprises tobermorite, xonotlite, and wollastonite.
4. The wet composition of claim 1 , wherein the water is deionized water.
5. The wet composition of claim 1 , wherein the composite material further comprises e-glass fiber in an amount ranging from 4% to 7%.
6. The wet composition of claim 1 , consisting of:
the composite material; and
the water, wherein the composite material consists of the synthetic hydrated calcium silicate and, optionally, e-glass fiber in an amount ranging from 4 to 7%.
7. A dry composition for extinguishing fires, comprising:
a composite material comprising a synthetic hydrated calcium silicate; and
water, wherein the dry composition comprises the composite material and the water at a ratio of 82% to 98% composite material:18% to 2% water, the composite material has a particle size ranging from greater than zero μm to 72 μm, and the synthetic hydrated calcium silicate has a density ranging from 60 kg/m 3 to 450 kg/m 3 .
8. The dry composition of claim 7 , wherein the synthetic hydrated calcium silicate has a density ranging from 90 kg/m 3 to 400 kg/m 3 .
9. The dry composition of claim 7 , wherein the synthetic hydrated calcium silicate comprises tobermorite, xonotlite, and wollastonite.
10. The dry composition of claim 7 , wherein the water is deionized water.
11. The dry composition of claim 7 , wherein the composite material further comprises e-glass fiber in an amount ranging from 4% to 7%.
12. The dry composition of claim 7 , consisting of:
the composite material; and
the water, wherein the composite material consists of the synthetic hydrated calcium silicate and, optionally, e-glass fiber in an amount ranging from 4% to 7%.