Elastomeric composition comprising graphene and tire components comprising said composition
Elastomeric composition for producing tire components comprising, based upon parts by weight per 100 parts by weight of rubber (phr): (A) 100 phr of a blend of rubber comprising at least 20% by weight of an isoprene polymer; (B) from 0 to 30 phr of silica; (C) from 0 to 50 phr of amorphous carbon black; (D) from 1 to 40 phr of graphene, wherein the graphene consists of graphene nanoplatelets, wherein at least 90% have a lateral size (x, y) from 50 to 50000 nm and a thickness (z) from 0.34 to 50 nm, wherein the lateral size is always greater than the thickness (x, y>z), and wherein the C/O ratio is ≥100:1.
1. An elastomeric composition comprising, based upon parts by weight per 100 parts by weight of rubber (phr):
(A) 100 phr of a blend of rubbers comprising a styrene-butadiene copolymer (SBR) and at least 20% by weight of an isoprene polymer;
(B) from 10 to 30 phr of silica having a BET surface area measured using nitrogen of from 40 to 600 m 2 /g;
(C) from 10 to 50 phr of amorphous carbon black; and
(D) from 2 to 30 phr of graphene,
characterized in that said graphene comprises nanoplatelets of graphene, wherein at least 90% of said nanoplatelets have a lateral size (x, y) from 500 to 15000 nm and a thickness (z) from 0.34 to 8 nm, wherein the C/O ratio is ≥100:1; and said nanoplatelets of graphene being at least one of i) free from surfactant or ii) comprising an amount of less than 1% by weight of surfactant deposited on the surface thereof;
wherein said elastomeric composition exhibits:
values of elastic modulus E′ at deformation rates from 0.01 to 10% that are from 25 to 55% higher than the values of elastic modulus E′ at the same deformation rates of the same elastomeric composition which does not comprise said graphene; and
a decrease of elastic modulus at a deformation rate of about 10% which is greater in the elastomeric composition comprising said graphene than the decrease of elastic modulus shown by the same elastomeric composition which does not comprise said graphene at the same deformation rate of about 10%.
2. The elastomeric composition according to claim 1 , characterized in that said graphene nanoplatelets of said component (D) have a C/O ratio ≥200:1.
3. The elastomeric composition according to claim 1 , characterized in that said component (A) also comprises a 1,3-butadiene polymer (PB).
4. The elastomeric composition according to claim 3 , characterized in that said isoprene polymer, said 1,3-butadiene polymer (PB) and said styrene-butadiene copolymer (SBR) represent at least 50% by weight of said component (A).
5. The elastomeric composition according to claim 1 , characterized by further comprising an ethylene-propylene-diene terpolymer (EPDM).
6. The elastomeric composition according to claim 5 , characterized in that said isoprene polymer and said styrene-butadiene copolymer (SBR) represent at least 50% by weight of said component (A), and said EPDM elastomer represents at least 30% by weight of said component (A).
7. The elastomeric composition according to claim 1 , characterized in that said component (B) comprises from 10 to 20 phr of silica, that said component (C) comprises from 15 to 40 phr of amorphous carbon black, and that said component (D) comprises from 4 to 10 phr of graphene nanoplatelets.
8. A tire component comprising an elastomeric composition comprising, based upon parts by weight per 100 parts by weight of rubber (phr):
(A) 100 phr of a blend of rubbers comprising a styrene-butadiene copolymer (SBR) and at least 20% by weight of an isoprene polymer;
(B) from 10 to 30 phr of silica having a BET surface area measured using nitrogen of from 40 to 600 m 2 /g;
(C) from 10 to 50 phr of amorphous carbon black; and
(D) from 2 to 30 phr of graphene,
characterized in that said graphene comprises nanoplatelets of graphene, wherein at least 90% of said nanoplatelets have a lateral size (x, y) from 500 to 15000 nm and a thickness (z) from 0.34 to 8 nm, wherein the C/O ratio is ≥100:1; and said nanoplatelets of graphene being at least one of i) free from surfactant or ii) comprising an amount of less than 1% by weight of surfactant deposited on the surface thereof;
wherein said elastomeric composition exhibits:
values of elastic modulus E′ at deformation rates from 0.01 to 10% that are from 25 to 55% higher than the values of elastic modulus E′ at the same deformation rates of the same elastomeric composition which does not comprise said graphene; and
a decrease of elastic modulus at a deformation rate of about 10% which is greater in the elastomeric composition comprising said graphene than the decrease of elastic modulus shown by the same elastomeric composition which does not comprise said graphene at the same deformation rate of about 10%.
9. The tire component according to claim 8 , wherein said component is a tread.
10. The tire component according to claim 8 , wherein said component is selected from the group consisting of: an inner tube, a tubeless tire, an inner liner of the tubeless tire, and a carcass of a bicycle tire.
11. The tire component according to claim 10 , characterized in that said component (D) comprises from 2 to 30 phr of graphene nanoplatelets.
12. The tire component according to claim 8 , wherein said graphene nanoplatelets of the component (D) have a C/O ratio ≥200:1 and are free from surfactants, functionalizing agents, and coupling agents.