Resin composition with polycarbonate resin, acrylonitrile-butadiene-styrene resin, and inorganic filler, resin molded article, method for manufacturing resin molded article, and electronic apparatus
A resin composition contains a polycarbonate resin, an acrylonitrile-butadiene-styrene resin, an elastomer, and an inorganic filler, in which, when the sum of the contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass, the content of the polycarbonate resin is 86 parts by mass or more and 96 parts by mass or less, the elastomer is an acrylic block copolymer, and the aspect ratio of the inorganic filler is 3 or more.
1. A resin composition comprising:
a polycarbonate resin, an acrylonitrile-butadiene-styrene resin, an elastomer, and an inorganic filler, wherein
when a sum of contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass,
the content of the polycarbonate resin is 86 parts by mass or more and 96 parts by mass or less,
the elastomer is an acrylic block copolymer,
an aspect ratio of the inorganic filler is 3 or more, and
a content of the inorganic filler is 72 parts by mass or more and 93 parts by mass or less.
2. The resin composition according to claim 1 , wherein
when the sum of the contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass, a content of the acrylic block copolymer is 2 parts by mass or more and 30 parts by mass or less.
3. The resin composition according to claim 1 , wherein
the inorganic filler is precipitated calcium carbonate or wollastonite.
4. A resin molded article comprising:
the resin composition according to claim 1 , wherein
the resin molded article is obtained by molding the resin composition.
5. The resin molded article according to claim 4 , wherein
the resin molded article has a continuous phase and a dispersed phase, and
at least one part of the dispersed phase contains the acrylonitrile-butadiene-styrene resin, the acrylic block copolymer, and the filler.
6. A method for manufacturing the resin molded article according to claim 4 , the method comprising:
mixing the polycarbonate resin, the acrylonitrile-butadiene-styrene resin, the elastomer, and the inorganic filler having an aspect ratio of 3 or more with each other to obtain a mixture in which the content of the polycarbonate resin is 86 parts by mass or more and 96 parts by mass or less and the content of the inorganic filler is 72 parts by mass or more and 93 parts by mass or less when the sum of the contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass;
melting and solidifying the mixture to obtain a resin of pellet-shaped particles; and
molding the resin of pellet-shaped particles by using a die.
7. An electronic apparatus comprising:
an exterior component having a resin molded article, wherein
the resin molded article according to claim 4 .
8. A resin composition comprising:
a polycarbonate resin, an acrylonitrile-butadiene-styrene resin, an elastomer, and an inorganic filler, wherein
when a sum of contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass, the content of the polycarbonate resin is 86 parts by mass or more and 96 parts by mass or less,
the elastomer is an acrylic block copolymer,
an aspect ratio of the inorganic filler is 3 or more, and
the inorganic filler is precipitated calcium carbonate or wollastonite.
9. The resin composition according to claim 8 , wherein
when the sum of the contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass, a content of the acrylic block copolymer is 2 parts by mass or more and 30 parts by mass or less.
10. A resin molded article comprising:
the resin composition according to claim 8 , wherein
the resin molded article is obtained by molding the resin composition.
11. The resin molded article according to claim 10 , wherein
the resin molded article has a continuous phase and a dispersed phase, and
at least one part of the dispersed phase contains the acrylonitrile-butadiene-styrene resin, the acrylic block copolymer, and the filler.
12. A method for manufacturing the resin molded article according to claim 10 , the method comprising:
mixing the polycarbonate resin, the acrylonitrile-butadiene-styrene resin, the elastomer, and the inorganic filler having an aspect ratio of 3 or more, the inorganic filler being precipitated calcium carbonate or wollastonite, with each other to obtain a mixture in which the content of the polycarbonate resin is 86 parts by mass or more and 96 parts by mass or less when the sum of the contents of the polycarbonate resin and the acrylonitrile-butadiene-styrene resin is set to 100 parts by mass;
melting and solidifying the mixture to obtain a resin of pellet-shaped particles; and
molding the resin of pellet-shaped particles by using a die.
13. An electronic apparatus comprising:
an exterior component having the resin molded article according to claim 10 .