Method for preparing multilayer of nanocrystals, and organic-inorganic hybrid electroluminescence device comprising multilayer of nanocrystals prepared by the method
Disclosed herein is a method for preparing a multilayer of nanocrystals. The method comprises the steps of (i) coating nanocrystals surface-coordinated by a photosensitive compound, or a mixed solution of a photosensitive compound and nanocrystals surface-coordinated by a material miscible with the photosensitive compound, on a substrate, drying the coated substrate, and exposing the dried substrate to UV light to form a first monolayer of nanocrystals, and (ii) repeating the procedure of step (i) to form one or more monolayers of nanocrystals on the first monolayer of nanocrystals.
1. A photocurable composition comprising
a first photosensitive compound, and
nanocrystals surface-coordinated by a dispersant containing no photosensitive functional group but miscible with the first photosensitive compound, wherein the first photosensitive compound comprises a photoreactive functional group and at least one selected from the group consisting of alkylene, amide, phenylene, biphenylene, ester-derived, and ether-derived group, and wherein the first photosensitive compound is not chemically bound to a surface of the nanocrystals.
2. The composition according to claim 1 , wherein a surface of the nanocrystals is further coordinated with a second photosensitive compound, wherein the second photosensitive compound is the same or different from the first photosensitive compound, and the second photosensitive compound is selectively bonded to a linker including cyanide, SH, amine, a carboxyl group, or a phosphonic acid group.
3. The composition according to claim 1 , wherein the photoreactive functional group comprises a carbon-carbon double bond or an acrylic group.
4. The composition according to claim 1 , wherein the first photosensitive compound is a photopolymerizable monomer, a photopolymerizable oligomer, a photopolymerizable polymer, or a mixture thereof, and is selected from the group consisting of a compound having one or more acrylic groups and/or vinyl groups, an ester-based compound, an ether-based compound and a mixture thereof.
5. The composition according to claim 1 , wherein the first photosensitive compound is selected from the group consisting of a multifunctional acrylate-based compound having two or more acrylic groups and/or vinyl groups, multifunctional polyalkylene oxide, a polysiloxane-based compound having one or more acrylic groups and/or vinyl groups, and a mixture thereof.
6. The composition according to claim 1 , wherein the first photosensitive compound is selected from the group consisting of allyloxylated cyclohexyl diacrylate, bis(acryloxy ethyl)hydroxyl isocyanurate, bis(acryloxy neopentylglycol) adipate, bisphenol A diacrylate, bisphenyl A dimethacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, 1,3-butyleneglycol diacrylate, 1,3-butyleneglycol dimethacrylate, dicyclopentanyl diacrylate, diethyleneglycol diacrylate, diethyleneglycol dimethacrylate, dipentaerythirol hexaacrylate, dipentaerythirol monohydroxy pentacrylate, ditrimethylolprpane tetraacrylate, ethyleneglycol dimethacrylate, glycerol methacrylate, 1,6-hexanediol diacrylate, neopentyiglycol dimethacrylate, neopentyiglycol hydroxypivalate diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, phosphoric acid dimethacrylate, polyetyleneglycol diacrylate, polypropyleneglycol diacrylate, tetraethyleneglycol di acrylate, tetrabromobisphenol A diacrylate, triethyleneglycol divinyl ether, triglycerol diacrylate, trimethyloipropane triacrylate, tripropyleneglycol diacrylate, tris(acryloxyethyl)isocyanurate, phosphoric acid triacrylate, phosphoric acid diacrylate, acrylic acid propargyl ester, vinyl terminated potydimethylsiloxane, vinyl terminated diphenylsiloxane-dimethylsiloxane copolymer, vinyl terminated polyphenylmethylsiloxane, vinyl terminated trifluoromethylsiloxane-dimethylsiloxane copolymer, vinyl terminated diethyl siloxane-dimethylsiloxane copolymer, vinylmethylsiloxane, monomethacryloyloxypropyl terminated polydimethyl siloxane, monovinyl terminated polydimethyl siloxane and monoallyl-mono trimethylsiloxy terminated polyethylene oxide.
7. The composition according to claim 1 , wherein the nanocrystals are at least one selected from the group consisting of metal nanocrystal, Group II-VI compound semiconductor nanocrystal, Group III-V compound semiconductor nanocrystal, Group IV-VI compound semiconductor nanocrystal, and a mixture thereof.
8. The composition according to claim 1 , wherein the nanocrystals are comprised of two or more selected from the group consisting of metal nanocrystal, Group II-VI compound semiconductor nanocrystal, Group IV-VI compound semiconductor nanocrystal, and Group III-V compound semiconductor nanocrystal, and wherein the nanocrystal is present in a form of a simple mixture of the two or more, a fused crystal in which the two or more are partially present, or an alloy of the two or more.
9. A nanocrystal-polymer composite film prepared from the composition according to claim 1 .
10. The nanocrystal-polymer composite film according to claim 9 , wherein the nanocrystal-polymer composite film has two surfaces, and has a predetermined pattern on at least one surface thereof.
11. The nanocrystal-polymer composite film according to claim 9 , wherein the predetermined pattern includes a recessed and/or protruded shape, and wherein the predetermined pattern has a rectangular shape, a triangular shape, a trapezoidal shape, a cone shape, a prism shape, a pyramid shape or a combination thereof.
12. A display device comprising the nanocrystal-polymer composite film according to claim 9 .
13. The display device according to claim 12 , wherein the nanocrystal-polymer composite film is disposed between a light-guide plate and a prism sheet.
14. A method for manufacturing a nanocrystal-polymer composite film comprising:
(i) preparing a photocurable composition comprising a first photosensitive compound, and nanocrystals surface-coordinated by a dispersant containing no photosensitive functional group but miscible with the first photosensitive compound, wherein the first photosensitive compound comprises a photoreactive functional group and at least one selected from the group consisting of alkylene, amide, phenylene, biphenylene, ester-derived, and ether-derived group, and wherein the first photosensitive compound is not chemically bound to a surface of the nanocrystals;
(ii) applying the photocurable composition to a substrate to form a photocurable composition coating layer; and
(iii) exposing the photocurable composition coating layer to a light.
15. The method according to claim 14 , wherein the method further comprising:
treating the photocurable composition coating layer with a mold having a predetermined pattern to form the predetermined pattern on a surface of the photocurable composition coating layer before exposing to a light.
16. The method according to claim 14 , wherein a surface of the nanocrystals is further coordinated with a second photosensitive compound, wherein the second photosensitive compound is the same or different from the first photosensitive compound, and the second photosensitive compound is selectively bonded to a linker including cyanide, SH, amine, a carboxyl group, or a phosphonic acid group.
17. The method according to claim 14 , wherein the photoreactive functional group comprises a carbon-carbon double bond or an acrylic group.
18. The method according to claim 14 , wherein the first photosensitive compound is a photopolymerizable monomer, a photopolymerizable oligomer, a photopolymerizable polymer or a mixture thereof, and is selected from the group consisting of a compound having one or more acrylic groups and/or vinyl groups, an ester-based compound, an ether-based compound and a mixture thereof.
19. The method according to claim 14 , wherein the method further comprises:
repeating the application of the photocurable composition to a substrate to form a photocurable composition coating layer and the exposure of the photocurable composition coating layer to a light, two or more times, to form two or more layers of nanocrystal-polymer composite thin films.
20. The method according to claim 19 , wherein the method further comprises:
laminating the two or more layers of nanocrystal-polymer composite thin films.