Nonaqueous secondary battery porous film composition, nonaqueous secondary battery porous film, and nonaqueous secondary battery
A composition for a non-aqueous secondary battery porous membrane including inorganic particles and a particulate polymer, wherein a volume-average particle diameter d 0 of the inorganic particles is 0.1 μm or more and 1.0 μm or less, a weight ratio between the inorganic particles and the particulate polymer is within a range of 95:5 to 50:50, and a volume-average particle diameter d 1 of the particulate polymer and the volume-average particle diameter d 0 of the inorganic particles satisfy d 1 /d 0 >1; and a non-aqueous secondary battery including the same.
1. A composition for a non-aqueous secondary battery porous membrane comprising inorganic particles and a particulate polymer, wherein
a volume-average particle diameter do of the inorganic particles is 0.1 μm or more and 1.0 μm or less,
a weight ratio between the inorganic particles and the particulate polymer is within a range of 95:5 to 50:50, and
a volume-average particle diameter d 1 of the particulate polymer and the volume-average particle diameter do of the inorganic particles satisfy the following relational formula:
1.5≤ d 1 /d 0 ≤3.0.
2. The composition for a non-aqueous secondary battery porous membrane according to claim 1 , wherein
the volume-average particle diameter d 1 of the particulate polymer is 0.15 μm or more and 3.0 μm or less.
3. A porous membrane for a non-aqueous secondary battery, wherein the porous membrane is formed using the composition for a non-aqueous secondary battery porous membrane according to claim 1 .
4. A non-aqueous secondary battery comprising a positive electrode, a negative electrode, a separator, and an electrolyte solution, wherein
one or more of the positive electrode, the negative electrode, and the separator have the porous membrane for a non-aqueous secondary battery according to claim 3 .
5. A porous membrane for a non-aqueous secondary battery comprising inorganic particles and a particulate polymer, wherein
a volume-average particle diameter do of the inorganic particles is 0.1 μm or more and 1.0 μm or less,
a weight ratio between the inorganic particles and the particulate polymer is within a range of 95:5 to 50:50, and
a volume-average particle diameter d 1 of the particulate polymer and the volume-average particle diameter do of the inorganic particles satisfy the following relational formula:
1.5≤ d 1 /d 0 ≤3.0.
6. The composition for a non-aqueous secondary battery porous membrane according to claim 1 , wherein the glass transition temperature of the particulate polymer is 30° C. or higher.
7. The porous membrane for a non-aqueous secondary battery according to claim 3 , wherein the glass transition temperature of the particulate polymer is 30° C. or higher.
8. The non-aqueous secondary battery according to claim 4 , wherein the glass transition temperature of the particulate polymer is 30° C. or higher.
9. The porous membrane for a non-aqueous secondary battery according to claim 5 , wherein the glass transition temperature of the particulate polymer is 30° C. or higher.