Catalytically active particulate filter
The present invention relates to a particulate filter which comprises a wall flow filter of length L and three mutually different catalytically active coatings X, Y and Z, wherein the wall flow filter comprises channels E and A that extend in parallel between a first and a second end of the wall flow filter and are separated by porous walls forming surfaces O E and, respectively, O A , and wherein the channels E are gas-tightly sealed at the second end and the channels A are gas-tightly sealed at the first end, characterized in that the coating X is located in the porous walls, the coating Y is located in the channels E on the surfaces O E and the coating Z is located in the channels A on the surfaces O A .
1. Particulate filter for removing particulates, carbon monoxide, hydrocarbons and nitrogen oxides from the exhaust gas of internal combustion engines operated with a stoichiometric air-fuel mixture, which particulate filter comprises a wall flow filter of length L and three mutually different coatings X, Y and Z, wherein the wall flow filter comprises channels E and A that extend in parallel between a first and a second end of the wall flow filter and are separated by porous walls forming surfaces O E and O A , respectively, and wherein the channels E are sealed in a gas-tight manner at the second end and the channels A are sealed in a gas-tight manner at the first end, characterized in that coating X is located in the porous walls, coating V is located in the channels E on the surfaces O E and coating Z is located in the channels A on the surfaces O A ; and wherein
the coating X is located in the porous walls, extends over the entire length L of the wall flow filter, and contains lanthanum-stabilized aluminum oxide in an amount of 25 to 30% by weight based on the total weight of the coating X, palladium or palladium and rhodium, a first oxygen storage component comprising zirconium oxide, cerium oxide, yttrium oxide and lanthanum oxide in an amount of 25 to 35% by weight based on the total weight of the coating X, and a second oxygen storage component comprising zirconium oxide, cerium oxide, yttrium oxide and praseodymium oxide in an amount of 25 to 35% by weight based on the total weight of the coating X, and
the coating Y is located in the channels E on the surfaces O E , extends from the first end of the wall flow filter to 25 to 75% of the length L and contains lanthanum-stabilized aluminum oxide in an amount of 40 to 50% by weight based on the total weight of the coating Y, palladium or palladium and rhodium and an oxygen storage component comprising zirconium oxide, cerium oxide, lanthanum oxide and praseodymium oxide in an amount of 40 to 50% by weight based on the total weight of the coating Y, and
the coating Z is located in the channels A on the surfaces O A , extends from the second end of the wall flow filter to 25 to 75% of the length L and contains lanthanum-stabilized aluminum oxide in an amount of 50 to 60% by weight based on the total weight of the coating Z, palladium or palladium and rhodium and an oxygen storage component comprising zirconium oxide, cerium oxide, lanthanum oxide and yttrium oxide in an amount of 40 to 50% by weight based on the total weight of the coating Z.
2. Particulate filter in accordance with claim 1 , wherein the coating V extends from the first end of the wall flow filter over 25 to 61% of the length L of the wall flow filter.
3. Particulate filter in accordance with claim 1 , wherein the catalytically active coating Z extends from the second end of the wall flow filter over 25 to 61% of the length L ref the wall flow filter.
4. Particulate filter in accordance with claim 2 , wherein the sum of the lengths of the coatings Y and Z is less than the total filter length L.
5. Particulate filter in accordance with claim 1 , wherein each of the coatings X, Y and Z contains has palladium and rhodium with one or both of the palladium and rhodium fixed on one or more substrate materials and one or more of the oxygen storage components.
6. Particulate filter in accordance with claim 5 , wherein one or more of the coatings X, Y and Z contains barium oxide or barium sulfate.
7. Particulate filter in accordance with claim 6 , wherein coatings X and Y contain barium sulfate.
8. Particulate filter in accordance with claim 5 , wherein the one or more substrate materials are metal oxides with a BET surface area of 30 to 250 m2/g.
9. Particulate filter in accordance with claim 1 wherein both palladium and rhodium are present on at least one of the coatings X, Y and Z.
10. Particulate filter in accordance with claim 9 wherein both palladium and rhodium are supported on a common substrate in coating X.
11. Particulate filter in accordance with claim 9 having a total precious loading resulting in a ratio of palladium to rhodium of 5:1.