Resin composition, and molded article and film thereof

1. A resin composition for an injection molded article comprising an acrylic resin and a graft copolymer,

wherein the graft copolymer comprises an innermost layer, an inner layer, and an outer layer:

wherein the innermost layer is a hard polymer (A) comprising, as structural units, a monomer mixture (a) comprising 1 to 40 wt % of benzyl (meth)acrylate, 60 to 99 wt % of an alkyl methacrylate ester, 0 to 35 wt % of an alkyl acrylate ester, and 0 to 15 wt % of another monomer having a double bond and copolymerizable with the benzyl (meth)acrylate, the alkyl methacrylate ester, and the alkyl acrylate ester; and 0.01 to 10 parts by weight of a polyfunctional monomer per 100 parts by weight of a total amount of the monomer mixture (a),

wherein the inner layer is a soft polymer (B) comprising, as structural units, a monomer mixture (b) comprising 40 to 99 wt % of an alkyl acrylate ester, 1 to 60 wt % of benzyl (meth)acrylate, and 0 to 40 wt % of another monomer having a double bond and copolymerizable with the alkyl acrylate ester and the benzyl (meth)acrylate; and 0.1 to 5 parts by weight of a polyfunctional monomer per 100 parts by weight of a total amount of the monomer mixture (b),

wherein the outer layer is a hard polymer (C) comprising, as structural units, a monomer mixture (c) comprising 60 to 100 wt % of an alkyl methacrylate ester, 0 to 10 wt % of benzyl (meth)acrylate, and 40 to 0 w % of another monomer having a double bond and copolymerizable with the alkyl methacrylate ester and the benzyl (meth)acrylate and 0 to 10 parts by weight of a polyfunctional monomer (per 100 parts by weight of a total amount of the monomer mixture (c)), and

wherein, when the resin composition is molded to obtain a molded article having a thickness of 2 mm, the molded article has a haze of 1% or less.

2. The resin composition according to claim 1 , wherein the another monomer in the monomer mixture (c) is one or more selected from the group consisting of: an alkyl acrylate ester; an aromatic vinyl monomer; and an unsaturated nitrile-based monomer.

3. The resin composition according to claim 1 , wherein a polymer obtained by performing up to polymerization for forming the inner layer of the graft copolymer has an average particle diameter of 50 to 400 nm.

4. The resin composition according to claim 1 , wherein the acrylic resin has a glass transition temperature of 115° C. or higher.

5. The resin composition according to claim 4 , wherein the acrylic resin comprises at least one selected from the group consisting of: a glutarimide acrylic resin; a maleimide acrylic resin; a partially-hydrogenated styrene unit-containing acrylic polymer; an acrylic polymer having a cyclic acid anhydride structure; an acrylic polymer comprising 97 to 100 wt % of methyl methacrylate and 3 to 0 wt % of methyl acrylate; and an acrylic polymer containing a hydroxyl group and/or a carboxyl group.

6. The resin composition according to claim 1 , wherein the resin composition comprises, relative to 100 parts by weight of a total amount of the acrylic resin and the graft copolymer:

40 to 98 parts by weight of the acrylic resin; and

60 to 2 parts by weight of the graft copolymer.

7. The resin composition according to claim 1 , wherein when the resin composition is molded to obtain a molded article having a thickness of 2 mm, the molded article has a haze of 2% or less.

8. An injection molded article comprising the resin composition according to claim 1 .

9. The molded article according to claim 8 , wherein when the molded article has a thickness of 2 mm, the molded article has a YI value of 4 or less.

10. The molded article according to claim 8 , wherein when the molded article has a thickness of 2 mm, the molded article has a maximum phase difference of 300 nm or less.

11. A method for producing a resin composition for an injection molded article comprising an acrylic resin and a graft copolymer, the method comprising polymerizing the graft copolymer by multistage polymerization comprising the following polymerization stages (I), (II) and (III):

(I) obtaining a hard polymer (A) by polymerizing 100 parts by weight of a monomer mixture (a) comprising 1 to 40 wt % of benzyl (meth)acrylate, 60 to 99 wt % of an alkyl methacrylate ester, 0 to 35 wt % of an alkyl acrylate ester, and 0 to 15 wt % of another monomer having a double bond and copolymerizable with the benzyl (meth)acrylate, the alkyl methacrylate ester, and the alkyl acrylate ester; and 0.01 to 10 parts by weight of a polyfunctional monomer;

(II) obtaining a soft polymer (B) by polymerizing 100 parts by weight of a monomer mixture (b) comprising 40 to 99 wt % of an alkyl acrylate ester, 1 to 60 wt % of benzyl (meth)acrylate, and 0 to 40 wt % of another monomer having a double bond and copolymerizable with the alkyl acrylate ester and the benzyl (meth)acrylate; and 0.1 to 5 parts by weight of a polyfunctional monomer; and

(III) obtaining a hard polymer (C) by polymerizing, in the presence of the soft polymer (B), 100 parts by weight of a monomer mixture (c) comprising 60 to 100 wt % of an alkyl methacrylate ester, 0 to 10 wt % of benzyl (meth)acrylate, and 40 to 0 w % of another monomer having a double bond and copolymerizable with the alkyl methacrylate ester and the benzyl (meth)acrylate; and 0 to 10 parts by weight of a polyfunctional monomer;

wherein, when the resin composition is molded to obtain a molded article having a thickness of 2 mm, the molded article has a haze of 1% or less.